Electronics Forum | Fri Nov 07 15:57:56 EST 2003 | Marc Simmel
Are there specifications or recommendations for electro-deposited tin-lead plating thickness on austenitic stainless steel that would provide a shelf life of 1 year? 6 months? Would 2 to 3 microns (78 to 118 micro-inches) 90/10 tin-lead over 1.27 mi
Electronics Forum | Mon Feb 13 12:41:38 EST 2006 | masrimhd
Hello, I know for sure that using lead-free technology in conventional tin-lead machines makes a lot of problems. But I wonder if we can use conventional tin-lead alloy and components with a lead-free machine! Is it possible? Does this imply any s
Electronics Forum | Tue Apr 13 08:08:33 EDT 1999 | Rob Palson
We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to bu
Electronics Forum | Mon Apr 19 02:38:41 EDT 1999 | Brian Sloth Bentzen
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Thu Jul 10 08:48:06 EDT 2003 | Kris
Hi, What would you consider significantly different about lead-free on flex circuits than tin-lead of flex circuits ? Have you published your experiances that you encountered while changing over to lead-free solder paste from a tin-lead paste ? T
Electronics Forum | Sun Jan 18 10:13:59 EST 2004 | davef
Materials added to solder can change its appearance. For instance: * Gold in tin/lead solder is dull / grainy * Palladium in tin/lead solder is dull / grainy We do NOT advocate using visual appearance to define the appearance of a good and a bad so
Electronics Forum | Tue Aug 31 12:01:26 EDT 2004 | russ
Kris, this practice has gone on for years. I have never heard of any problems associated with this. I have heard "grumblings" about tin lead parts being processed with lead free paste, but have seen or heard of no data to support. Russ
Electronics Forum | Tue Oct 04 11:42:07 EDT 2005 | Bob Leible
I was wondering if anyone has studied the effects of tin lead solder in the wave. If we leave the same solder in the solder pot, how many COMPLETE cool downs and start ups can the solder go through before it begins to break down? Please let me know
Electronics Forum | Tue Oct 04 12:49:59 EDT 2005 | patrickbruneel
The amount of times the tin/lead solder can be melted and solidified is unlimited and the heat cycles do not affect the solder characteristics. The only reason for changing the solder pot is when impurities are at or over the maximum levels.
Electronics Forum | Wed Aug 27 07:13:05 EDT 2008 | eyalg
I need to solder SAC/HASL PC boards in a NON ROHS process (Tin Leaded solder paste and profile + Tin leaded components) Can I do that?? Regards, Eyal