Electronics Forum | Fri Oct 08 08:26:03 EDT 1999 | Carol Zhang
| | | I have a board, 4 spacers needed to be soldered on the board | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, ther
Electronics Forum | Thu Oct 07 16:57:02 EDT 1999 | Glenn Robertson
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Fri Nov 25 05:16:44 EST 2016 | slavek
Hello, I want to ask on suitable temperature profile for PCBs with ENIG final surface finish. I know that it is complex question with many unknowns. When the PCB will be standard 1,5 mm 35/35 Cu and the amount of components will have any influence o
Electronics Forum | Tue Dec 12 01:52:05 EST 2006 | hemu_me
As we have vitronics oven(SMR610A) made in dec,1997,which has 5 heating zones and 2 cooling zones. For Lead free soldering what should be our baseline for low/medium boards.we have gathered profiles from various paste manufacturers,however we don't k
Electronics Forum | Tue May 12 22:57:30 EDT 2009 | davef
Polyimide bare board with tin over nickel solderability protection.
Electronics Forum | Thu Jan 27 14:49:53 EST 2000 | Glenn Robertson
Tuan - One of the reasons I suggested pre-tinning (aside from the negative effects of Gold on appearance and reliability) is the known slower wetting of Sn/Ag and Sn/Cu alloys as compared to Sn/Pb. If you don't have to be Lead-free, the high Lead
Electronics Forum | Fri Sep 21 10:44:34 EDT 2001 | slthomas
You can, and for small parts you probably won't see much difference between body temp. and lead temp. For QFPs or PLCCs there will be a much greater delta, though. I'd be more concerned with the small surface area you're making contact on (spherica
Electronics Forum | Tue Feb 27 18:16:42 EST 2001 | davef
I have never seen excess tin [heard of it, just never seen it]. Excess lead yes, but tin no. See, tin oxidizes faster than lead. This means that dross has a higher tin content than the solder in the pot. So, with a very high dross machine, we regul
.gif)