Electronics Forum | Tue Jun 25 22:22:22 EDT 2019 | proy
We have an electrovert 16" econopak wave solder machine with two identical pots (exchange between Tin Lead and Lead Free). When the pots are exchanged the same thermocouple is used, and the same controller is used - with the set point adjusted. The S
Electronics Forum | Tue May 31 11:56:12 EDT 2005 | chunks
Hi Matt, Get definitive answers! Contamination on the HASL finish?: From the pix you posted, it looks like something fishy is going on. I�d reject them back to the board house and demand an answer. Most board houses and purchasing people will g
Electronics Forum | Fri Jul 02 05:28:13 EDT 1999 | Vinesh gandhi
| | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design).
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 10:06:17 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Sat Nov 03 10:57:27 EDT 2012 | davef
EricR: Regarding "*** By the way, since we have used the Tin-Silver-Copper lead free solder there has been a strange liquid type chemical leek from the oven exhausted pipes." ... I don't know anything about your process, but the first thing I'd inve
Electronics Forum | Thu Oct 26 21:48:57 EDT 2017 | deanm
For selective soldering I would first look at the alloys your products require. Do you run tin-lead, lead free or both? If you run (or may run in the future) two alloys, then look for a machine that has quick change solder pots. Secondly, do your bo
Electronics Forum | Sun Apr 04 10:16:16 EDT 2004 | cyclopsn
I'm involved in backplane manufacturing process. There are about 10 electrolitic capacitor assembled in my board.These capacitor are soldered using a selective soldering machine. My problem is that these capacitor will charged up and failed as short
Electronics Forum | Thu Jul 22 22:18:12 EDT 2004 | davef
Notes from an AIM No-Lead Presentation ... Wave Soldering * May require a higher pot temperature than tin/lead: 255-265*C * May require a change in liquid fluxes to compensate for the poor wetting of some alloys and high thermal stresses of the wave
Electronics Forum | Mon May 17 20:39:49 EDT 2004 | Ken
I disagree about the maintenance issues with tin/copper solder. All high tin content solders are hard on machines (silver or not). More dross? Controlling the back flow, front flow velocity and AVOID constant surface cleaning will reduce your dros