Electronics Forum | Wed Nov 30 15:15:34 EST 2016 | warwolf
Any lead free will eat a leaded designed wave soldering machine. But SN100c will eat it the slowest, our soldering tips used to only last 3 months with SAC305 when we changed to SN100c solder wire we are having around 9 months tip life. Our wave sol
Electronics Forum | Mon Feb 13 13:26:21 EST 2006 | pjc
If you're asking about wave solder machine, yes you can run Sn/Pb in a "Pb Free" machine. The concern is that when its time to run Pb Free you're going to have to remove all the parts from the solder pot to remove all the Pn/Pb solder residue from po
Electronics Forum | Tue Jun 08 12:49:41 EDT 1999 | Dave F
| Hi,my master | How to iron out such soldering bridge with below conditions: | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | 3.using spraying fluxer and n
Electronics Forum | Tue Jun 08 13:06:53 EDT 1999 | Kevin Hussey
| | Hi,my master | | How to iron out such soldering bridge with below conditions: | | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | | 3.using spraying fl
Electronics Forum | Tue Jun 08 17:52:53 EDT 1999 | Chrys Shea
| | | Hi,my master | | | How to iron out such soldering bridge with below conditions: | | | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | | | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | | | 3.using s
Electronics Forum | Tue Oct 04 20:31:16 EDT 2016 | davef
IPC-7721, Section 6.1, Jumper Wires, Jumper Wire Selection #5 states: "Recommended wire is solid, insulated, plated copper wire, 22 to 32 AWG with a heat resistant insulation. Wire with tin-lead plating may be restricted due to environmental laws."
Electronics Forum | Wed Dec 24 15:28:17 EST 2008 | edmentzer
We use SN100C for wave soldering and hand Lead free soldering and have had very good results. The wire cored solder for hand soldering flows good and makes very good solder joints. The SN100C in the wave solder machine also works very good. We use
Electronics Forum | Fri Oct 16 14:36:11 EDT 1998 | Jeff Sanchez
| With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to overco
Electronics Forum | Wed Jul 06 07:02:27 EDT 2005 | davef
Try: * A-610D, 6.3 � Wire / Lead Preparation - Tinning * J-STD-001D, [There is probably something. We'll look later.]
Electronics Forum | Thu Dec 28 15:40:13 EST 2006 | fredericksr
The fluxes involved with lead-free soldering tend to be more aggressive and the tip deterioration is a side effect of making the world a greener place. I am not certain if any of the tip manufacturers claim to have lead-free resistant tips. I would