Electronics Forum | Wed Jun 30 12:14:40 EDT 1999 | John Thorup
| | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). I
Electronics Forum | Fri Mar 13 16:38:57 EDT 2009 | hegemon
'Hege is checking in for the DRS25 by Air Vac. Forced Air Convection reflow, and huge heating capacity for bottom side, ensuring minimum Delta T across the PCB during the process. Have 3 of these machines constantly in use for the last 2 and a half
Electronics Forum | Mon Dec 12 13:18:22 EST 2005 | Kris
Hi Samir can you post some pictures of the whiskers ? I would also recomend you post your pictures on the IPC listserve forum for lead-free where you will find a focussed group that will be very interested in your pictures. http://listserv.ipc.or
Electronics Forum | Fri Oct 14 16:45:14 EDT 2011 | proy
I have a wave solder machine I am replacing, it is full of tin lead 63/37. I would like to sell off in 100lb lots. A certificate of composition will be provided. Price is $6.50/lb not including shipping from Toronto Canada. 100lb lots minimum
Electronics Forum | Tue Aug 07 01:19:49 EDT 2012 | reypal
Thanks DucHoang, More input: 1. Tin/Lead s.paste on Pbfree component 2. Machine pick and place 3. Reflowed@ 210-230C peak @ around 15sec. 4. Boards are subjected to washing process 5. This issue can be seen after washing process. Do you think it
Electronics Forum | Thu Jan 27 20:17:25 EST 2022 | stephendo
What exactly counts as "always on"? Our ROHS wave solder machine is always on during the week but the pot shuts off at the end of the shift and turns on early in the morning so that the solder is melted before we get to work. It is only using a small
Electronics Forum | Thu Apr 19 08:50:38 EDT 2007 | rgduval
Welcome to RoHS. Or, at least, to the version of RoHS that I've had to deal with since I started with my current company. Blowholes and pinholes seem to be common in PB-free manufacturing. At least, they have for me here. I also note that IPC has
Electronics Forum | Mon Jan 31 05:25:54 EST 2005 | gaurav
Morning All, > > I have to choice between two > axial through hole machines: Panasert AVK 3 and > Universal VCD Sequencer 8. I will insert axial > components with 0,45 mm to 0,8 mm component lead > diameter and perform jumper wire insertion in t
Electronics Forum | Mon Jul 17 13:37:35 EDT 2006 | carln
Here is something I copied from Circuitnet.com. This appears to answer your question and then some... http://www.circuitnet.com/experts/ Ask the Experts Jul 17, 2006 What type of cleaner method is preferred for lead-free stencils? What type of s
Electronics Forum | Thu Jul 20 16:28:55 EDT 2000 | Bob Willis
Most robust wave soldering machines will cope with lead free alloys. The temperatures in air that we have run has been between 260-265C. In my opinion the dross generation has not been significantly effected. I was doing a workshop for a well known
.png)