Electronics Forum | Tue Sep 22 12:25:31 EDT 1998 | Chrys
| | Hi Jacqueline! | | Do these joints that you're having problems with happen to be on fine pitch solder joints? Are the fillets staying attached to the foot and separating from the pads cleanly? | | If that is true, are there many vias concen
Electronics Forum | Thu Aug 06 09:51:20 EDT 1998 | Bob Willis
This text may be of interest to any one with tin lead spots Guide to Solder Spots - A New Plague in Manufacture ? So what are solder spots ? They appear to be the next big problem in modern reflow assembly in fact in any process that involves solder
Electronics Forum | Thu Jun 04 12:05:43 EDT 1998 | Anthony
Dear Dave, I have a "possible" solution to your problem, though I have never tried it myself. If you're trying to come up with a non-abrasive technique for removing solder-keep reading. If it's a faster method you desire, do yourself a favor and hi
Electronics Forum | Wed May 27 21:05:30 EDT 1998 | Steve Gregory
Hey yooze guys! Enough of the jokes between you and Earl (GRIN), let's get back to the topic...well, okay... you can tell a few more...(but good ones, 'kay?) Anyhoo...I'm not sure if ya'll are on the IPC Technet list or not, I've not seen any posts f
Electronics Forum | Tue May 19 05:42:36 EDT 1998 | Earl Moon
| Earl, | I admit that I missed your article since I seemed to have let my subscription to Circuit Fabrication Magazine expire. I am interested in your experience in this area. Is there a way to get a copy of your paper? Could you maybe post it to
Electronics Forum | Wed Dec 05 17:23:41 EST 2001 | davef
Now there�s a conundrum. You want the �best way to clean leads�, but you want to use the worst type of flux for cleaning leads. You say, �20% copper exposed� � * What happened to the solderability protection during this two-year storage? Wouldn�t
Electronics Forum | Thu Jan 08 16:16:09 EST 2004 | Dean
My first concern would be the choice of solder paste you have. There are better chemistries out there that far exceed the capabilities of the 609 2. Yes, the part will partially float on the solder (assuming plastic qfp). Cross sectioning would sho
Electronics Forum | Sun Feb 13 15:23:03 EST 2005 | Mike Konrad
There are several manufacturers of batch-format de-fluxing systems. Here is a list of them: Aqueous Technologies http://www.aqueoustech.com (909) 944-7771 Batch and Inline UnitDesign http://www.unitdesign.com (714) 672-9944 Batch Austin American T
Electronics Forum | Sun Mar 12 01:58:44 EST 2006 | grantp
Hi, We have been soldering lead free BGA's onto products with lead based paste, and we have had no increase in defects at all. We have used a standard lead paste profile, so we are not altering the temps anything from what's recommended by the paste
Electronics Forum | Thu Mar 23 22:26:53 EST 2006 | Joseph
Dear all, Referring comment from Mr. Jack,IPC director certification & assembly technology, the term "fillet tearing" is too broad. Cracks or fractures in the required fillet area, with SnPb or LF alloy and whether you call it tearing or not, is a D