Electronics Forum | Sun Sep 15 21:44:41 EDT 2002 | jason
Hi Dave, Immersion Ag has poor surface appearances after reflow or rather tarnished, while Immersion Tin requries higher temp. Probably that's why Immersion Ag is more preferred.
Electronics Forum | Fri Nov 07 18:26:05 EST 2003 | jsloot
Is anyone using .062 aluminum circuit boards with copper conductors in your production lines? What kind of reflow profile is required? What special considerations are there to be looking for? I am asking for any information you can give me. Thanks
Electronics Forum | Tue Apr 09 16:19:37 EDT 2002 | Peter L.
Has anyone built using the ALIVH PCB (0402, 0.8mm pitch uBGA) on the SMT line? I would like to know any process issues (paste printing, p&p, reflow) related to processing this pcb. Specifically, what type of solder paste was used (no clean) and wha
Electronics Forum | Fri Jul 28 08:08:18 EDT 2006 | Chunks
Screen printer, placement machine(s) and oven. You may also need a hand insertion line, selective solder or wave soldr and some form of electrical test. There are a ton of name brands that no two people can agree on. To get a better feel for what
Electronics Forum | Thu Sep 10 15:06:11 EDT 2009 | dyoungquist
My guess is that he is talking about the gold plated pads not fully wetting with solder. We have seen this on some of our ENIG boards with the gold still showing at the far corners of the rectangular pads. Not knowing if this is hand soldering or p
Electronics Forum | Fri Oct 24 06:55:48 EDT 2008 | clampron
Good Morning WS, If you experieced the solder balls after reflow of a bare board through the oven, then the source of the solder is either the oven or the board. I have had boards with untented via's that were HASL'd that had entrapped solder and fl
Electronics Forum | Sat Jul 26 11:17:31 EDT 2008 | manishc
i am facing problem of pcb track lifing at B.G.A. after reflow.we r using lead free paste and fr-4 grade pcb with peak temp.about 270 deg.
Electronics Forum | Thu Oct 30 19:59:05 EDT 2008 | gregoryyork
solder ball was caused by hasl process not reflow. seen before many times, look around wells of smt on bare boards should be more of them
Electronics Forum | Thu Oct 23 23:38:48 EDT 2008 | pathakvj
We have 8 layer HASL PCB. We saw molten solder blobs / balls on op side of assembled PCB. (to check, if this was a bare board problem), We passed bare board as received thru, SMT reflow oven and saw solder balls on top side of board. What could be th
Electronics Forum | Wed May 04 10:42:55 EDT 2005 | nice90
Handling a PCB 1. Check your ESD slippers and ESD Strap first before entering the SMT production line 2. A PCB manufactred over 90 days must be stored first on the baking Oven before Production 3. Temperature on the Baking oven must be 125plus and m
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
winsouce.jpg)