Electronics Forum: tombstone defecte (Page 1 of 17)

solving tombstone

Electronics Forum | Fri Aug 01 02:10:26 EDT 2008 | fowlerchang

Pad design is not only the size of pad but also the distance between two pad. N2 will increase tombstone as we tested. 10 zones reflow oven and slow temperature ramp will reduce this defect. MustII is the equipment which is used to test the solderabi

TOMBSTONE DEFECTS

Electronics Forum | Tue Mar 11 09:49:59 EST 2003 | MGARCIA

DO YOU KNOW? WHAT KIND OF SOLDER PASTE IS BETTER IN ORDER TO AVOID THE TOMBSTONE DEFECT IN SMT PROCESS.

Minimizing Tombstoning Defects

Electronics Forum | Mon Sep 17 10:09:45 EDT 2001 | martys

What variables that you have tested are sensitive to producing tombstoning defects and what advice can you provide to minimize them?

Nitrogen gas and Tombstone defect

Electronics Forum | Mon Nov 21 10:12:11 EST 2011 | callckq

All, I try to find explanation(Article)on how Nitrogen gas can make tombstone defect even worst. However, I can't find one in the net. Anyone that has this information or article, appreciate if you can share with me...Thanks in advance.

TOMBSTONE DEFECTS

Electronics Forum | Sun Apr 13 19:57:51 EDT 2003 | Thomas

I saw some specifications on the Tamura RMA-012 FP stating that it counters tombstoning...hope it helps you problem...

Tombstone defect

Electronics Forum | Sun May 04 22:10:20 EDT 2003 | Thomas

Did u ever try a anti-tombstone solder paste to try to eliminate this problem ??

Tombstone defect

Electronics Forum | Wed May 07 09:24:33 EDT 2003 | davef

Kris The majority of our tombstoning in very small passive SMT is caused by imperfections in end-cap solderability protection plating.

Minimizing Tombstoning Defects

Electronics Forum | Tue Sep 18 10:22:22 EDT 2001 | jschake

Paste Flux / Reflow: Our experiments indicated that the combination of no-clean solder paste and air forced convection reflow produced the fewest tombstone defects, followed by water-soluble paste reflowed in air, and most tombstones occurring with

TOMBSTONE DEFECTS

Electronics Forum | Fri Apr 04 05:02:08 EST 2003 | alexyalung

Hi All, The best solution we made on our tombstone defects is component Z dimension set at pick and place machine. Usually for 0402 components Z height is pre-set by the machine at 0.5 mm, by reducing it to 0.35mm we have solve our tombstone problem

Nitrogen gas and Tombstone defect

Electronics Forum | Tue Nov 29 14:57:45 EST 2011 | jlawson

Sorry on N2 and tombstone, many other aspects cause tombstones and n2 in itself does not cause tombstones. It can help make other bad variables tip over edge to cause tombstones more than with no N2. Get these right then N2 is not issue.

  1 2 3 4 5 6 7 8 9 10 Next

tombstone defecte searches for Companies, Equipment, Machines, Suppliers & Information

Software for SMT

World's Best Reflow Oven Customizable for Unique Applications
Void Free Reflow Soldering

We offer SMT Nozzles, feeders and spare parts globally. Find out more
SMT feeders

High Precision Fluid Dispensers
SMT feeders

High Throughput Reflow Oven
Circuit Board, PCB Assembly & electronics manufacturing service provider

Software programs for SMT placement and AOI Inspection machines from CAD or Gerber.
PCB separator

Internet marketing services for manufacturing companies