Electronics Forum | Wed Dec 15 18:03:28 EST 2004 | russ
I have used both 4 and 5 mil stencils for 10 mil round apertures. We don't have volume measurement capability but we measure height and the 4 mil appeared to have more paste and better uniformity from a visual standpoint than the 5 mil. The unfortu
Electronics Forum | Mon Apr 09 13:28:06 EDT 2001 | slthomas
I've been wondering if I was the only person thinking this. There are so many print parameters that are programmable now on new machines (squeegee pressure, height, speed, snap-off settings, cleaning intervals) that the process would (in my oh-so-hu
Electronics Forum | Thu Jul 19 09:56:52 EDT 2001 | Damian Holzmann
The obvious difference between 2D and 3D is that an accurate volumetric measurement can only be obtained with a 3D measuring system. Laser line measurement in 2D does not allow accurate volumetric measurement. If you modify the aperture in a stencil
Electronics Forum | Wed Sep 18 06:53:05 EDT 2002 | CH
1) For solder short, pls check the paste height. Too much vol will cause short. For 15 mils use 5 mils thickness stencil if possible. Check profile preheat time to prevent hot slumpof the paste. 2) type 4 powder will be better for 15 mils pit
Electronics Forum | Fri Oct 18 22:32:20 EDT 2002 | mdm4ua
If you have room try putting a small piece of tape on the bottom of the stencil right next the aperture that is giving you the problem. The added height of the tape (Kapton tape is usually about 3 mils thick) will likely give you a heavy enough depo
Electronics Forum | Mon Jun 13 01:31:36 EDT 2005 | buchi79
Devef, The stand off height is 75micron. We only clean the product after underfill process. Dispense epoxy under the FC & cure it before aqueous wash. Samples are sent for LPC (liquid particle count) Test to ensure cleaniness. By the way, our plant
Electronics Forum | Thu Apr 20 14:33:18 EDT 2006 | dirk29
We had that problem with our printers we just drill and tap the top end of the stop and put a short screw in to allow us to adjust the top height of the stop and catch the board. Be careful not to make it to long or to could restrict the board from l
Electronics Forum | Wed Jun 07 22:33:50 EDT 2006 | Bolos
first: what is your problem after reflow? second: a good rule of thumb is a tolerance of 1 mil. for example..if you got 5 thou stencil thickness then your range of thickness is 6-/+1 thou.. then you just improve after you get your height data and ana
Electronics Forum | Wed Mar 27 07:01:26 EDT 2019 | charliedci
200uM seems high. I say this because typically our solder stencils in this application are between 80uM and 100uM thick which would leave the component height less than that after reflow. However if your not experiencing any shorting between pads I w
Electronics Forum | Thu Oct 27 06:05:50 EDT 2022 | angela t
SMT chip processing short-circuit bad phenomenon mostly in the fine pitch IC pins, mostly in the 0.5mm and the following pitch between the IC pins, because its spacing is small, improperly designed template or printing a slight omission is very easy