Electronics Forum | Wed Jan 23 06:12:36 EST 2019 | tirthkar8980
Dear Team, Need help, we are trying to make urea core solder wire but the problem is some time core remains partially empty no urea filling in solder wire. please help me how to solve this problem. thank you, Tirthkar
Electronics Forum | Mon Nov 01 16:22:47 EDT 2010 | jax
Who Cares... Mix Away! Although you should not mix different Solder Pastes' together in a container or on a stencil (Mostly due to the flux, although solder sphere size and shape could cause an issue), mixing solder brands or chemistries on a board
Electronics Forum | Wed Aug 26 05:57:45 EDT 2009 | aw126901
Hi We have recently noticed that our lead free solder wire is being supplied with expiry dates (typically 2-3 years after manufacture). I have seen "date of manufacture" information on wire before but I was not aware that a cored solder wire could e
Electronics Forum | Fri Jun 25 12:19:52 EDT 2010 | operator
I have always been under the impression that you want the flux make-up of your cored wire and supplemental flux (squeeze bottle) to be as identical/compatible as possible. I was just looking over a manufacturers datasheet for a resin-based cored wir
Electronics Forum | Fri Oct 16 14:36:11 EDT 1998 | Jeff Sanchez
| With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to overco
Electronics Forum | Wed Feb 14 17:16:23 EST 2001 | slthomas
From Kester's web site: "Flux cored solder wire has a limited shelf life determined by the alloy used in the wire. For alloys containing more than 70% lead, the shelf life is two years from date of manufacture. Other alloys have a shelf life of thr
Electronics Forum | Fri Oct 16 21:17:04 EDT 1998 | Scott McKee
| | With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to over
Electronics Forum | Thu Jul 25 12:25:54 EDT 2019 | davef
In “J-STD-001 Rev G Amendment 1 Process Qualification” Debbie Carboni, Global Product Line Manager, KYZEN Corp, Nashville, TN said: What change constitutes a need for requalification? Major/ Level 1 – Flux or flux-bearing materials (e.g. flux, so
Electronics Forum | Sat Aug 01 12:06:52 EDT 2009 | isd_jwendell
Unfortunately, I don't see any image. If your part will survive 300C then even convection reflow should work. The use of paste and reflow ovens are for when you move to production quantities. It sounds like you could hand solder your prototypes (proo
Electronics Forum | Thu Mar 23 10:15:57 EDT 2017 | solderingpro
Rob, That is where Bob works. ------------------------------------------------------- There are many companies that exist offering multiple different products and procedures for cleaning pcb assemblies. I agree, in my practice, most companies str
winsouce.jpg)