Electronics Forum | Wed Jan 23 06:12:36 EST 2019 | tirthkar8980
Dear Team, Need help, we are trying to make urea core solder wire but the problem is some time core remains partially empty no urea filling in solder wire. please help me how to solve this problem. thank you, Tirthkar
Electronics Forum | Wed Mar 17 21:42:19 EST 1999 | Chuck Garth
We are presently aluminum wirebonding to gold plated lands. Our board manufacturer has been very inconsistient in the quality. It seems as though theey are over etched by about half the amount they should be. Can anyone give me the spec's that normal
Electronics Forum | Tue May 13 07:40:14 EDT 2014 | sarason
There are many alloys of silver solder for higher temperatures mostly used in plumbing There are also alloys which are available in paste form used in the manufacture of hybrids. sarason
Electronics Forum | Thu Sep 04 21:50:47 EDT 2003 | davef
We like to use "enameled wire" that can be stripped by hot solder. Formvar [105�C] will not do that. Formvar was designed to with stand the hot oil seen in transformers. So, it requires either chemical or mechanical stripping. Most polyurethanes
Electronics Forum | Mon Aug 27 15:06:29 EDT 2001 | davef
This otta push Wolfgang over the top ... Recommended reading G.G. Harman, Wire Bonding in Microelectronics : Materials, Processes, Reliability, and Yield, 2nd edition, McGraw-Hill Electronic Packaging and Interconnection Series, 1997. G.G. Harman, R
Electronics Forum | Wed Aug 26 05:57:45 EDT 2009 | aw126901
Hi We have recently noticed that our lead free solder wire is being supplied with expiry dates (typically 2-3 years after manufacture). I have seen "date of manufacture" information on wire before but I was not aware that a cored solder wire could e
Electronics Forum | Fri Oct 16 14:36:11 EDT 1998 | Jeff Sanchez
| With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to overco
Electronics Forum | Wed Apr 17 03:37:29 EDT 2019 | mahammansoor
Hi, I work in a Cable and Wire manufacturing company. We are currently working on an order of Automotive wires that require strict RoHS compliance. What are the RoHS compliance strategies that we can implement at the production line (PVC and Copper
Electronics Forum | Fri Oct 16 21:17:04 EDT 1998 | Scott McKee
| | With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to over
Electronics Forum | Mon Nov 01 16:22:47 EDT 2010 | jax
Who Cares... Mix Away! Although you should not mix different Solder Pastes' together in a container or on a stencil (Mostly due to the flux, although solder sphere size and shape could cause an issue), mixing solder brands or chemistries on a board