Electronics Forum | Sun Apr 10 03:25:35 EDT 2005 | Peter
Normally, some conformal coatings do not have very good wetting properties, that should be basic function of a good coating material (the same reqirement as avoid bubbles during coating process)! For UV curing conformal coatings, you can try Lackwe
Electronics Forum | Wed Aug 17 22:41:37 EDT 2005 | davef
Peter are you having fun with solder masks erwat? We saw this years ago with LPI solder masks. It shows occasionally with other masks. We agree with Russ. If nothing [eg, alcohol, flux thinner, acetonitrile, or water] dissolves the haze, then it
Electronics Forum | Fri Dec 18 09:27:51 EST 2009 | sforman1
Tom: Once again - why are you using solvent based conformal coating. 1B31 is OK as a CC but it contains Toluene and MEK!! It is only 35% solids which means you are trying to get rid of 65% solvent. If you must use it due to customers requirement then
Electronics Forum | Tue Feb 19 08:08:29 EST 2013 | williamaxler
My company is starting to look into Conformal Coating Equipment. From preliminary talks it sounds like we would like to use a UV material. I have a few question I was hoping as a group you all would be able to pass along some insight. 1. Do any of
Electronics Forum | Wed Nov 28 07:44:33 EST 2001 | stefwitt
Justin, you will find measuring equipment at http://www.omega.com All sensor signals are in uV or mV and require a signal amplifier. If you get an amplifier with display, you can program a conversion factor for mV to board stretch and it will show a
Electronics Forum | Tue Mar 21 20:33:09 EST 2000 | Dave F
Shane: We don�t dispense, but we have thought about it. Several points about peelable solder masks in a no-clean (low residue) process: � Beware of latex peelable solder mask with a low res process without extensive testing. The problem is usuall
Electronics Forum | Thu Jan 28 15:43:16 EST 1999 | Dave F
| Hello Netters, | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solde
Electronics Forum | Thu May 10 09:08:20 EDT 2012 | blnorman
Thickness wet or after cured?
Electronics Forum | Thu May 10 13:30:42 EDT 2012 | umar
Hi Norman... the coating need to measure at wet and after cure condition.
Electronics Forum | Thu Jan 28 15:53:12 EST 1999 | Dave F
| | Hello Netters, | | | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI