Electronics Forum | Sat Aug 25 08:39:15 EDT 2007 | gsala
If plastic Carrier Tape (CT)/ emboss tape, is made by: a)Polycarbonate material, it can withstand temperature around 120C� or may be more mantaining original dimension. b)Polystirene material, at max 45�C-50C� the CT starts to change dimensions and
Electronics Forum | Fri Nov 02 12:01:26 EST 2001 | mparker
I have two cases where I must bake after DI wash. The moisture entrapment is specifically within microprocessor sockets. Without air gun blow out and baking, oxidation occurs that causes flaky contacts for the PGA. We will bake for 2-3 hours @ 60C. O
Electronics Forum | Thu Nov 01 00:32:14 EST 2001 | ianchan
we bake boards 80~120 deg-C @1hr, after in-line DI wash. oven setting to 90 deg-C, as +/-5 deg-C, tolerance against door open/shut fluctuations = "temperature loss". If anyone has evidenced procedure, that shows no need for baking, pray do share wi
Electronics Forum | Thu Nov 01 01:48:14 EST 2001 | hamos_wks
168hrs, 1week of storage and frequently applied for rework after testing.
Electronics Forum | Tue Oct 30 21:42:32 EST 2001 | surachai
I have question about board baking after in line washing machine then I would like to know some information that ; 1) Do we need board baking after in line washing machine? Both bare board and assembly borad normally we don't bake . 2)In case of ne
Electronics Forum | Thu Nov 01 17:36:20 EST 2001 | davef
We don�t bake between routine washing between soldering cycles. We bake when we immediately go to test or box-build. Certainly, it all depends on your process, materials, and boards. So, how did you determine that you needed to spend the money? I
Electronics Forum | Fri Aug 16 18:23:48 EDT 2002 | kenbliss
Hi Dave Interesting points. If I understand you correctly 1. about 2% of part numbers have a moisture problem 2. Packaging frequently comes in with expired dates on them. This seems hard to believe you would accept them. 3. To really solve the
Electronics Forum | Thu Jul 12 02:15:53 EDT 2012 | thmeier
Check also the specs / recommendations of your PCB manufacturer. We bake boards 4h/120°C before reflow and after automated cleaning (it´s not FR4!) and also if we have to rework with the autometd rework- stations (massive IR underheating ,..). Regar
Electronics Forum | Wed Jul 11 22:48:54 EDT 2012 | joeion
It is correct to remove moisture in PCB by baking. But I think the time and temperature is too little. According to our experience, it should be more than 60min at 120 centigrade degrees.
Electronics Forum | Thu Jul 05 21:07:09 EDT 2012 | davef
Probably they had a problem with a certain product, tried baking, the problem went away and ever since there stuck with this money loosing process. So, ... * Write up a plan to split a couple of batches, bake a portion of each batch, don't bake the o