Electronics Forum | Wed Nov 17 09:28:40 EST 1999 | Steve Z
Hello, I am new to the SMT area and I need to know what a "good" vapor phase reflow profile should look like. The fluids we are using have a BP of 45 C and 219 C. Thanks,
Electronics Forum | Fri Nov 19 05:12:21 EST 1999 | Graham Naisbitt
Steve, If you can get me your snail-mail address, I will send you some latest information. We actually have a totally new system called Delta 5. It is Condensation Soldering rather than Vapour phase, the difference being that we solder in an air ti
Electronics Forum | Fri Jul 16 15:30:22 EDT 1999 | SMTASSY
Perhaps a little hard to find but is there anyone who uses a vapor phase process to solder populated card with BGAs. I am interested in the success rate of such a process. It is obvious that the throughput is reduce vs a convection oven but still thi
Electronics Forum | Wed Mar 12 15:26:46 EDT 2014 | dan_ems
Hello, in my SMT process I have some problems with the solderability (look like dewetting) on a PCB with finish HASL Lead Free with a composition that is melt at 230 degree Celsius. My oven is with vapor phase and the peak temperature is 230 degre
Electronics Forum | Thu Mar 13 14:12:31 EDT 2014 | davef
You're creating a new alloy on the surface of your board. The alloy will have a melting point determined by the constituent metals of the alloy. Your alloy consists of: * Lead-free HASL solderability protection on the board * Lead-free solder paste *
Electronics Forum | Mon Jul 19 11:11:18 EDT 1999 | Wolfgang Busko
| Perhaps a little hard to find but is there anyone who uses a vapor phase process to solder populated card with BGAs. I am interested in the success rate of such a process. It is obvious that the throughput is reduce vs a convection oven but still t
Electronics Forum | Mon Jul 19 12:37:15 EDT 1999 | Wolfgang Busko
| | | | | Hi, SMTASSY | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | First, we do not do real series produktion, only prototyping up to som
Electronics Forum | Tue Jul 20 05:29:14 EDT 1999 | Wolfgang Busko
| | | | | | | | Hi, SMTASSY | | | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | | First, we do not do real series produktion, only prototypi
Electronics Forum | Mon Feb 23 14:44:08 EST 2009 | sunny
Are boards produced using Vapor phase ovens dirtier than N2 Reflow oven. Are there any studies/papers someone can point to? if not what are the methods to verify this? is IPC specified SIR test using 24B SIR test coupons? please advise. thanks in adv
Electronics Forum | Mon Aug 16 20:19:10 EDT 2004 | Grant
Hi, We have both Vapor Phase ASSCON semi auto as well as Soltec convection inline ovens. I must say we had no end of problems with Vapor Phase. We tried everything, and just could not totally eliminate tomb-stoning completely. We would always get a