Electronics Forum | Tue Aug 22 16:46:31 EDT 2006 | Steve
Using Interflux IF2005, Have electrovert as well as new Novastar Topside of board temp is 265F solder bath 275c. I assume applying via foam fluxer. Not sure.
Electronics Forum | Mon Feb 26 20:02:42 EST 2001 | davef
First, I don�t understand why your board fabricator can�t do a good job plugging your vias. Additionally, when you consider that they forgot to plug the first batch of boards, it makes me wonder if they are desirable as a supplier. Generally, we us
Electronics Forum | Fri Sep 04 02:09:03 EDT 2009 | sachu_70
Hi Walter, Do you refer to a sprayfluxer operation? The problem seems to be a parameter setting issue. 1. Ensure the wide angle spray reaches PCB with optimum jet pressure. You could pass a glass plate to understand flux coverage and view Jet pressur
Electronics Forum | Thu Jan 06 08:03:47 EST 2005 | davef
On solder in vias: It looks like the via are not solder masked well and pick-up solder either: * Solder coating ... OR * During leveling It's possible that the design specifies openings in the solder mask for these via. On solder in the unsupporte
Electronics Forum | Fri Oct 13 05:21:08 EDT 2000 | Robert Steltman
Looking at the original post, it seems that the white residue is formed on the board after wave soldering and becomes evident when it has been left standing for a while. From what I understand, it seems that the solids content of the "no clean" flux
Electronics Forum | Mon Sep 23 12:59:12 EDT 2013 | pauldavis4
New pcba supplier sent us first article pcbas (SMT, Wave & hand solder operations) that failed our testing due to no-clean flux residues found under ICs and around passive capacitors. Second lot came in and had 100% pass yield, but we still see a cl
Electronics Forum | Fri Jun 08 17:22:51 EDT 2007 | naynayno
We have been producing an IMS assembly with SMT dpak's for some time. However, we recently encountered a new problem by chance - the parts can be flicked off with a finger nail. I state by chance because the solder joints are wetted and shiny with
Electronics Forum | Fri Oct 05 07:31:29 EDT 2001 | furrer
When tenting vias almost a few vias are not covered completly by Solder Mask. Does this one side open vias affect the Immersion Tin Process ? Do we get chemical residues in the vias ?
Electronics Forum | Tue Aug 26 21:12:24 EDT 2003 | iman
depends if your water wash process is manual or automation? important is the water residue inside the via holes is adequately blown out. As long as the water-flux residue is out, testing down the line should not be a issue, at least from theory and o
Electronics Forum | Thu Jan 07 12:55:19 EST 2010 | scottp
Did someone repair that solder joint to the left of the vias with plumber's flux and leave the residue?