Electronics Forum | Mon Aug 16 11:36:23 EDT 2004 | soease
Hi everybody, now that lead-free is coming, I'm looking forward to change the oven we own in company I work for. Eternal question: what's the best oven technology on market. I allready know that we won't work with IR ovens, but I would like to have
Electronics Forum | Mon Aug 16 13:31:45 EDT 2004 | Dreamsniper
We do not have problems with preheating. before we used to suspect that the cause of tombstone was that because the semi-auto and manual version do not have pre-heat stage. We had 1 with an IR heater and it is quite okay. you can use it too to cure a
Electronics Forum | Tue Aug 17 11:03:36 EDT 2004 | Bernard Mulcahy
Hi , I am having an issue with my Mydata TP11 UFP. About 2 yrs ago I upgraded from TPSYS 1.6 to TPSYS 2.2.4 to enable me to use the agilis feeders. This involved an operating system change from Venix (Unix Clone) to a version of Linux. the upgrade i
Electronics Forum | Wed Aug 18 06:20:42 EDT 2004 | Bernard Mulcahy
Thanks for the Feedback -- Yes the hard-disks is taking a dump -- This will be the fourth new hard drive since I did the upgrade from Tpsys 1.6 to Tpsys 2.2 Mydata can't really come up with a reason --I can't believe that I am just being 'unlucky' g
Electronics Forum | Wed Aug 18 09:05:52 EDT 2004 | Stefan Witte
With this many hard drive problems, I would search in other directions. You may have a defective power supply or a bus switch on the motherboard. I would dump the entire computer. With Linux you have to be a bit more selective in the components. I wo
Electronics Forum | Mon Aug 23 14:49:36 EDT 2004 | msjohnston1
I have no experience working with the systems you listed about, however I have experience working with a GSI Lumonics SVS systems measuring solder paste. I am also in the process in looking for new equipment to replace the GSI systems that is capabl
Electronics Forum | Mon Aug 30 16:31:34 EDT 2004 | aburgos
Mike: When you stated that you are looking for a different AOI to replace GSI Lumonics because of 0201 solder paste inspection. Does that mean that you have a 1X scanner and it is not giving you reliable results? Have you tried the 2X scanner from G
Electronics Forum | Tue Aug 31 02:15:12 EDT 2004 | AOI Solution
I need to address the issue for colorful display on solder joints, for whoever researched on this machine, no one can deny it is a smart feature for visual assistance. however, it is still Mono color "gray scale" algorithm. it basically "paint" the i
Electronics Forum | Tue Aug 17 17:06:43 EDT 2004 | davef
First, we'd like to see your supplier's minimum Sn thickness to be increased to 10um. Look here for support of this position: http://www.psma.com/HTML/FILES/forums/leadfree/hp_ext_pos_sn_for_pbfree.pdf Second, increasing the thickness of tin: * Ra
Electronics Forum | Fri Aug 20 07:20:18 EDT 2004 | rlackey
Hi, We've got a 6622, been running since Jan & does a good job. You may want to consider the smart wave option as this will (allegedly)force solder up the holes to give you better joints for lead free. Spray fluxer works very well, limiting the am