Electronics Forum | Fri Oct 19 11:51:25 EDT 2007 | rgduval
By definition, no clean solder can be not-cleaned. The solder/flux are formulated to result in low ionic-contamination, hence, no cleaning. I have, however, always had at least one customer that requests their no-clean solder get cleaned. No-clean
Electronics Forum | Fri Oct 26 07:41:26 EDT 2007 | bbl
We recently changed to an Amtech no clean paste and flux that is washable. So far excellent results. Far superior to the water soluable paste we were using. Fewer solder balls, longer life in printer, boards can be left up to 5 days and still come
Electronics Forum | Fri Oct 19 16:24:53 EDT 2007 | jmelson
Really, if you start out from the beginning planning to clean the boards, then DON'T use the no-clean flux! The way that stuff is made, it leaves a hard, low-solubility residue that takes a LOT of effort to get clean. If you plan to clean, use a wa
Electronics Forum | Mon Oct 22 15:41:39 EDT 2007 | davef
Bruno The real question about your troop using Kester 951 wave solder flux on boards is: how is the flux applied and controlled. See, when you apply this flux with your wave solder fluxer, it is ideally applied in a metered fashion with your fluxer
Electronics Forum | Tue Nov 02 08:36:51 EDT 2010 | rgduval
Michelle, Our experience with no-clean solder pastes has been that water washing a mis-print is a bad idea. We've found that DI water does not do a sufficient job removing the no-clean paste (the same goes for stencils). Instead, we have washed no
Electronics Forum | Tue Nov 02 07:50:18 EDT 2010 | babe7362000
I just need a clarification on NC254 No clean solder paste. If we have parts on the bottom side of the board that already are soldered and we go to run the other side of the board and it was misprinted, is it ok to run thru the washer? I just need
Electronics Forum | Thu Aug 28 11:31:17 EDT 2008 | patrickbruneel
Matt solder mask finishes gives the widest process window in view of potential amount of residues when using No-Clean. Shiny (glass like) finishes are more sensitive to residues due to lower surface area compared to matt finish. If the shiny finish i
Electronics Forum | Wed Feb 26 23:59:48 EST 2003 | Mike Konrad
Grant, No-Clean paste + IPA = White Residue! #1: Stop using IPA #2: Switch to either a solvent-based de-fluxing chemical or an aqueous-based de-fluxing chemical. If you are using an ultrasonic cleaner for your boards as stated, do not use sapon
Electronics Forum | Tue Sep 21 02:51:06 EDT 1999 | Mohammed saad
Thank you all for your help. about your question Wolfgang, I am using no-clean solder paste from Kester. Mohammed | | Hi all, | | | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we ne
Electronics Forum | Mon Sep 20 09:02:34 EDT 1999 | Wolfgang Busko
| Hi all, | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are TH, the S