Electronics Forum | Fri Dec 16 10:25:37 EST 2005 | solderiron
Rather than cleaning a water soluble flux residue off the board, by encapsulating the product. covering the board or the component with lets say a Hysol encasulant. Would this prevent the active flux residue from migrating and deteriorating the elect
Electronics Forum | Fri Dec 16 11:21:18 EST 2005 | patrickbruneel
Steve, Water-soluble fluxes are per definition very corrosive and need to be cleaned (read the data sheet) Encapsulation will prevent humidity reaching the water-soluble acids but will not prevent reducing the metals the flux is in contact with to m
Electronics Forum | Fri Dec 01 14:12:50 EST 2000 | Jim M.
My company currently uses water soluble paste for our SMT process. We were having trouble retaining hot water in our in line, closed loop DI cleaner. The cleaner kept shutting down when the water temp. dropped below 125C. As a result, the conveyor
Electronics Forum | Wed Jan 03 10:56:46 EST 2001 | Mike Konrad
Hi Dave, Water soluble flux has two opposite attributes. #1: It is the easiest flux to remove. #2: It is the worst flux to leave behind on a board. As for # 1, there are many de-fluxing systems out there that are very capable of removing water
Electronics Forum | Mon Apr 29 10:42:47 EDT 2002 | Jim M.
I had problems with white residues on both WS609 and WS 3060.The WS 3060 turned out to be a carbonized material.The composition after analysis (Energy Dispersive X-ray spectrum) turned out to be tin,tin,phosphore and cloline and tin. Alpha also have
Electronics Forum | Tue Feb 23 16:45:36 EST 2010 | dyoungquist
Davef is right on as usual. We are doing exactly what you do. Some smt with no clean paste then the plate through connectors on our selective solder machine using water soluble flux. We then clean with a ultrasonic water process. We do see the re
Electronics Forum | Fri Sep 15 09:24:54 EDT 2000 | C.K.
At my last place of employment, that was the big reason why nobody (especially the Design Engineers) bought into a no-clean process - interference with high-impedance circuits. One guy was so paranoid about flux residues remaining on the board, that
Electronics Forum | Fri Dec 01 15:37:50 EST 2000 | Dason C
Jim, you may need to look with different paste instead of the cleaning solvent. Please advise what is the paste which you currently using? Beside, when you talking about the board stayed in hot area, is it a drying area or the cleaning zone. If it
Electronics Forum | Fri Dec 01 16:02:33 EST 2000 | Jim M
Thanks for your reply. I 've tried to clarify and answer your questions. The water soluble paste used is WS3060, type 4. The boards are sent through a inline di cleaner after reflow. There is a hot Di waterwash, rinse and then hot air to dry the wa
Electronics Forum | Mon Apr 29 04:57:28 EDT 2002 | madreindeer
Hi, That is very common in WS pastes.It is white residue (Salt) Usually it�s not dangerous it only looking bad. I think best way would be contact your paste supplier and they should know what would take a stain off if not, change supplier. There i
.gif)