Electronics Forum | Mon May 07 11:25:21 EDT 2007 | colormaker
Flux foam is not affected by board or pallot. This wave is not the same as the hollis I used. The hollis wave flowed from middle to left and right side. This wave only flows to the left and its a very slow wave. Jerry
Electronics Forum | Mon Jul 29 18:57:17 EDT 2002 | pzohbon
Does anyone know where to find information for wave temp profiling? pzohbon
Electronics Forum | Mon May 07 15:08:09 EDT 2007 | davef
What is a smart way to determine that the solder in the wave pot is moving at the same speed as the board?
Electronics Forum | Mon May 07 12:11:33 EDT 2007 | colormaker
I have the option of increasing the wave pump but when I do the wave is very unstable. Do you have the possibility to create a backflow at the wave to drain the oxides away from the board? Not sure how to do this I wish I have the old 1962 7' holl
Electronics Forum | Mon May 07 12:40:08 EDT 2007 | patrickbruneel
Jerry, At the end of the article in the link you will see how the wave needs to look like. http://www.interfluxusa.com/Technical/No-Residue_implementation.htm This wave design has been adopted by most machine manufacturers and I would be surprised
Electronics Forum | Fri Jan 28 12:30:57 EST 2005 | glenda
We are looking for a used or new wave machine must be able to do lead free solder. Does anyone have contact information in the Chicago, il area for used wave soldering machines? Thanks for any help we can get.
Electronics Forum | Fri Nov 11 04:13:23 EST 2005 | arnold
we are manufacturer of molded type transformer and we soldered are units using wave soldering machine and then we washed the units to remove flux residue. what materials or any process for us to eliminate the process of washing after wave soldering.
Electronics Forum | Mon May 07 13:06:35 EDT 2007 | colormaker
Thank you all for your help. I will fire up the wave again Friday to test another run. Keep the comment flowing its been a great help. Anyone suggest a solder wave system for running 40 boards an hour ? Jerry
Electronics Forum | Mon Jul 29 19:21:58 EDT 2002 | davef
Look to: * Your flux supplier's recommendations to baseline your recipe [similar to using your paste supplier's recommendations for setting your reflow recipe] * 7530 'Guidelines for Temperature Profiling for Mass Soldering (Reflow and Wave)' for gui