Electronics Forum | Fri Jun 12 11:15:50 EDT 1998 | Ryan Jennens
Hey all! The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pallet w
Electronics Forum | Mon Jun 12 10:57:51 EDT 2000 | Jason
I am new to wave soldering. Any information is greatly welcomed. Here is the problem. After soldering the boards they have a film on the bottom of them and sometimes a white powder looking substance. I have tried decreasing the amount of flux on
Electronics Forum | Mon Sep 28 19:07:47 EDT 1998 | Steve Gregory
| I have had some field failures returned recently, the boards had flux contamination under the components in a sensitive area, Nothing really visible until the component was removed, and the board had no evidence of rework of any type. Is it poss
Electronics Forum | Thu Mar 17 03:07:17 EST 2005 | Chua
Hi, We are running lead free at wave solder now and the spray flux system is down. If we are going to able the flux manually, what problem will we be facing with the excess flux able. Appreciate for the advise.
Electronics Forum | Wed Aug 27 14:58:21 EDT 2008 | omid_juve
we have problem in setting the density of a no clean flux for using before wave soldering . first we dilute the flux but we have many short circuit problem between the pads of edge connector,then we densify the flux all the short circuit is removed b
Electronics Forum | Mon Apr 26 20:14:48 EDT 2021 | goldendragon
Hello gen, Is there any recommendation of a liquid flux for SN100 solder bar on wave? Appreciates!
Electronics Forum | Thu Aug 28 12:18:03 EDT 2008 | grics
Why yes, I regognize all the best. WML, I have an idea... I am going to call it, the Dunker. Instead of anyone foaming, I will get the wave operators to throw the boards into a rubbermaid tub full of flux/gasoline mixture and send through to the wav
Electronics Forum | Tue Sep 02 14:59:41 EDT 2008 | hermes
if two boards with different solder masks give different results on flux residue level after soldering with the exact same machine settings than it is clear that one of the solder masks is not compatible with your no-clean flux. could be the solder m
Electronics Forum | Thu Aug 28 11:31:17 EDT 2008 | patrickbruneel
Matt solder mask finishes gives the widest process window in view of potential amount of residues when using No-Clean. Shiny (glass like) finishes are more sensitive to residues due to lower surface area compared to matt finish. If the shiny finish i
Electronics Forum | Thu Aug 28 09:30:20 EDT 2008 | patrickbruneel
Omid, No-clean fluxes need to be used right out of the can without thinning. In the past with RA and RMA fluxes you could adjust or thin them to your desired density because they had plenty of solids up to 30%. No-Clean fluxes have a lot lower solid
winsouce.jpg)