Electronics Forum | Fri Mar 06 15:46:57 EST 2009 | deeclaybrook
Hi We have anew material that is very cost effective for solder pallets called Electro-Lock. You may find out more at http://www.rapidtool.com Kind regards dee claybrook
Electronics Forum | Sun Feb 22 08:23:57 EST 2009 | davef
On a wave solder pallet, we'd expect the metal parts that go through the pallet to be warmer than the pallet material, but we don't expect them to be warmer than the solder. We don't expect a well made board to blister at soldering temperature. So,
Electronics Forum | Tue May 16 11:58:27 EDT 2006 | jsloot
What is the best or ideal cleaning method for wave solder pallets? I have been using iso prop and am not sure if this is the cause for having brittle wall material. I wouldn't think alcohol would degrade the durastone material. Most of my pallets hav
Electronics Forum | Tue Sep 11 12:56:03 EDT 2007 | jsloot
Can anyone give me any information on the longivity of titanium insert wave pallets. What I am looking for is the integrity of thin walls over several hundred cycles and the interface between the insert and the durostone material.
Electronics Forum | Fri Feb 24 04:36:30 EST 2006 | rlackey
Hi Ken, There may be different composites of Durastone, but there are certainly mixes out there that are. http://www.ascenteceng.com/resources/materials.html We used durastone as a carrier for flex circuits as well. Cheers, Rob.
Electronics Forum | Wed Feb 22 14:47:09 EST 2006 | jsloot
I have been looking at wave pallets with titanium inserts. I was told about another more recent and less expensive insert using aluminum. The aluminum is coated with some sort of material to prevent the solder from sticking. Is this anodized? Does an
Electronics Forum | Wed Feb 22 16:42:47 EST 2006 | Mark Beesley
Hello John, There are some coatings for aluminum to eliminate solder drag out. The do not work with all fluxes it is called hardcoat anodized it is black or geen in color. Unless you have faily high volumn the hard coat cost can be as high as titan
Electronics Forum | Fri Feb 20 02:09:23 EST 2009 | nibirta
Hi all, I have a question regarding some wave pallets having metallic traces of Titanium. The solder mask is blistering in some locations on the PCB and I am wondering if this Titaniumn may have an influence by incresing locally the temp. Also we ar
Electronics Forum | Mon Feb 23 05:37:23 EST 2009 | emmanueldavid
Necoleta, PWB Blistering/De-lamination may not be due for Titanium finished threads / holders which is typically being used to draw high Shelf Life of Pallets and even flow across Auto Wave Soldering rails. There is also nothing to suspect on Liquid
Electronics Forum | Mon Feb 23 05:46:26 EST 2009 | nibirta
thk you very much for your fast answers. And yes, I am suspecting the same things also. The problem is to convince the PCB supplier that is his fault. A big fight all the time. SO, i will double check everything you said, and I willl come back with r