| | | | Hi Folks, | | | Need to draw upon the vast expertise in this forum... | | | Whenever you fill a new wave solder machine with fresh bar solder, it seems to produce more than the normal amount of dross for a few weeks. I always understood thi
Electronics Forum | Tue Oct 18 19:34:02 EDT 2011 | warwolf
so there is no one here baised in New Zealand that wants to buy our SAC305 solder dross and recycle it, we have about 120KG at the moment, anyone intrested?
Electronics Forum | Wed Oct 19 11:33:15 EDT 2011 | caerleon
easier if you recycled on-site? You can still send off for reclaimation the oxide powder that your left at the end of the process. Failing that talk to your supplier to see if they have arrangements to do this for you or look at reducing dross - i f
Electronics Forum | Wed Oct 19 20:04:06 EDT 2011 | warwolf
yeah I’ve tried to go down the road of internal recycling but the company carnt justify spending 20k on a machine that does it. Ah but where still onto it in other places though our SMT department has very minimal wastage on solder paste as we have b
Electronics Forum | Fri Oct 28 21:46:35 EDT 2011 | rdh_41
Hi , I'm interested in Tin and hoping to open long-term business relationship with your company. We are Taiwan-based company dedicate in Tin (Sn). We are looking for opportunity to work with you. And it would be great if you have large quantity of t
Electronics Forum | Tue May 17 10:11:54 EDT 2005 | russ
I would use a foam fluxer since spraying rosin will make the stickiest nastiest mess you can imagine. 18 layer board huh? You will want convection preheat, both top and bottom preheaters, preheat tunnel of at least 4-5', a chip wave, laminar flow w
Electronics Forum | Mon Jun 12 14:03:12 EDT 2000 | MikeF
Jason, First, check with the manufacturer of the flux you are using. They can tell you what board topside temperature range the flux is designed for. Some other info is needed for the residue part. Is it showing up on the same board, or different boa
Electronics Forum | Wed Aug 02 12:04:42 EDT 2017 | davejohnson
Hopefully not too late of a reply... We currently have both, the Ersa ETS 330 (running LEAD solder) and Seho GoWave 1030 (RoHS solder). Bought the Ersa used, and it seems like a strong built industrial high volume machine. We've needed to modify it a
Electronics Forum | Fri Jan 25 11:49:09 EST 2008 | toddl
Hi all, I have an inconsistent situation. Lately, we seem to have excessive dross buildup in the solder pot which inturn causes the pot to overflow. Has anyone had a similar experience? Here are the details: age of machine= 9 years, flux used= Kester
Electronics Forum | Tue Nov 21 22:15:59 EST 2000 | Vince Whipple
Mohammed, The first suggested place to start with your question would probably be with your flux Mfr. Push them! The quantity of dross is effected by several factors: The higher your solder pot temp., the higher your dross level... but don't go too