Electronics Forum | Mon May 25 21:10:28 EDT 2009 | padawanlinuxero
Hello !! I have a problem with my wave solder oven, in one of the products we made has connectors on one side of the pcb and in the other one has SMT components the process is kinda tricky on the SMT components we use an adhesive and put to the refl
Electronics Forum | Sat Jan 29 16:35:33 EST 2000 | Robert Steltman
We have a Seho wave soldering machine and cannot seem to get rid of dross that is being generated within the solder pot, and is being pumped out in the wave. It is not the same kind of dross that forms on the surface of the solder pot(this is very m
Electronics Forum | Mon Jan 31 12:24:24 EST 2000 | Dave F
Robert: Several points: 1 Dross is a mixture of various things with no "fixed" composition: � The obvious things are metal oxides mixed with metal and this can vary in color with temperature and composition - remember some intermetallic oxides form
Electronics Forum | Mon Oct 19 05:16:56 EDT 2015 | florintoma
Hello all, I have a problem with the wave 6622c . The temperature of solder pot and preaheating zones 1 and 2 is not increasing. the strange thing is that the machine is not display no error. Can you help me with some advices?? regards
Electronics Forum | Tue Oct 20 10:14:59 EDT 2015 | aemery
Florin, Not sure if this will be helpful or not, but I have completed a couple of pot height retrofits for these waves and I seemed to remember that one of my clients spilled some solder and shorted out the 24vdc power supply. I am pretty sure this
Electronics Forum | Thu Feb 26 16:49:57 EST 1998 | specnor tecnic corp
we have some rebuilt wave soldering systems in stock ready to be shipped. epk-ii smt with lambda wave, chip wave ,omega wave. 4 preheaters,jacking stand roll out computer control. machine is in a great shape. another machin upk15f with 6 preheaters
Electronics Forum | Mon Sep 03 06:17:19 EDT 2007 | mun4o
hi, This is moisture problem, I think.I have similar problem.You must try to bake PCBs.I bake our PCBs in solder wave mashine , under solder pot.There T is about 80*C - after 6-8h the PCB is dry regards
Electronics Forum | Wed Aug 29 02:21:42 EDT 2007 | jgrootkoerkamp
It is a lead free process with sac305. We use goldfinish FR4 boards. Preheat is between 110 and 115 degrees. I am sure it is a moisture problem because longer stored boards have more blowholes. What is the maxium period to store the boards without
Electronics Forum | Thu Sep 06 16:58:40 EDT 2007 | gregoryyork
are you sure it isnt down to an hygroscopic contaminant causing the problem.I've only ever seen it once or twice in gold,really quite unusual.Its not too much gold brightner or similar residue.If it can be cleaned off then it shouldnt be there so it
Electronics Forum | Tue Aug 28 06:17:11 EDT 2007 | jgrootkoerkamp
I have problems with blowholes during the wave soldering process. I already find out that the stock time between reflow and wave is the most important. The longer the boards are in stock the more blowholes we have. We don't have a climat controlled
winsouce.jpg)