Electronics Forum | Thu May 11 18:59:40 EDT 2000 | lboone
Have anyone perform wave soldering on FR-2 and FR-1 printed circuit board with lead free soldering? Can you share the parameters(wave temperature,preheat temperature, contact time, wave height,etc,) used and did you do any changes to the wave solderi
Electronics Forum | Wed Dec 03 01:36:35 EST 2008 | lococost
Is anyone wave soldering 0603 leadfree succesfully? We have no problems soldering them leaded, but lead free we see a lot of random skips and some shorts. We use SAC. We have tried different fluxes, flux settings, playing around with preheat, sol
Electronics Forum | Fri Dec 05 02:50:16 EST 2008 | lococost
So, no one is wave soldering 0603 succesfully? Not even teh wavemaster??
Electronics Forum | Wed Dec 10 05:06:20 EST 2008 | gregoryyork
Great as most Lead Free machines have the wrong angle on them 7 degrees is correct. So you are still exiting the wave in the middle of the pot then.
Electronics Forum | Fri Dec 05 11:27:10 EST 2008 | patrickbruneel
Every problem faced with (all) lead free alloys can be solved with 2 words �add lead� I'll keep it short don't want to sound like a broken record.
Electronics Forum | Fri Dec 05 13:47:22 EST 2008 | wavemasterlarry
looks like my knowldge preceeds me again. I woud try a different flux. If it doesn't work - it will take a question mark away and your one step closer to total success.
Electronics Forum | Tue Dec 09 19:04:54 EST 2008 | gregoryyork
you need to check your angle on this, can you measure and advise what you have cheers Greg York
Electronics Forum | Wed Dec 10 01:56:12 EST 2008 | lococost
The angle is a standard Soltec 7deg. We don't have the tools to measure this accuratly, but I do trust Soltec on this.
Electronics Forum | Tue Feb 21 15:25:05 EST 2006 | masrimhd
I have no experience, but you can find some possible tricks to upgrade your wave machine into a good lead free one at: http://www.comtreeinc.com/documents/lead-free-wave-soldering.pdf
Electronics Forum | Tue Feb 21 15:09:11 EST 2006 | russ
Read your flux data, it will answer all of your questions