Electronics Forum | Thu Nov 04 11:56:33 EST 1999 | Tim Almy
Is 260 degrees C / 500 degrees F the optimum temperature for wave soldering ?
Electronics Forum | Thu Nov 04 15:57:46 EST 1999 | Dave F
I'm with John. Back in the old MIL-2000 days, the pot temperature was 245-275C (475-525F). Now, 240-260C (460-480 F) is more accepted for eutechic (eutechicish) solder. My2� Dave F
Electronics Forum | Mon Apr 16 12:59:51 EDT 2001 | Mike R
If you will place a temperature strip on the board during wave soldering process you will get a max of 210 F or 98.8 C which is normal on the standard wave temperature. The problem on the 10% solder on the TH via hole can be caused by insufficient fl
Electronics Forum | Thu Nov 04 14:13:34 EST 1999 | John Thorup
Hi Tim It sort of depends on the solder alloy being used and the particular assemblies being soldered. If you are using the usual 63/37 alloy I would consider 500 to be a bit warm unless the assembly required it. Some alloys would require a higher
Electronics Forum | Tue Nov 09 10:35:02 EST 1999 | WilDaly
Tim, I try to get 2-3 degrees C/sec (bottomside) rise on my boards through wavesolder. I like to get the topside to about 90-95 degrees C, but this is the optimum temp for the flux that I am using. To fast of a slope and you will burn your flux of
Electronics Forum | Sat Apr 14 03:25:04 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Sat Apr 14 03:25:10 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Fri Nov 05 21:41:46 EST 1999 | chartrain
Temperature vs time is what soldering is all about. The faster you run your conveyor, the more heat will have to come from the pot for a given assembly. Example: You heat the board to 200F top side through the preheaters. Eutectic 63/37 melts at 361.
Electronics Forum | Sat Apr 14 00:04:21 EDT 2001 | zam_bri
I'm not a Wave soldering guy and my friend have asked me a question on what is the best preheat time and temperature for Wave soldering.They experiences only 10% flow up thru the PTH barrel. I've asked them to increase the temperatue to 120 Deg C. Cu
Electronics Forum | Fri Nov 11 06:58:03 EST 2005 | bk
A little more information on your current wavesoldering process would be helpful in helping you. Information like what kind of flux your are using,how you are applying the flux,what preheat temps you are using,and your conveyor speed. Without knowing
winsouce.jpg)