Electronics Forum | Mon Jul 29 19:21:58 EDT 2002 | davef
Look to: * Your flux supplier's recommendations to baseline your recipe [similar to using your paste supplier's recommendations for setting your reflow recipe] * 7530 'Guidelines for Temperature Profiling for Mass Soldering (Reflow and Wave)' for gui
Electronics Forum | Fri Nov 25 05:16:44 EST 2016 | slavek
Hello, I want to ask on suitable temperature profile for PCBs with ENIG final surface finish. I know that it is complex question with many unknowns. When the PCB will be standard 1,5 mm 35/35 Cu and the amount of components will have any influence o
Electronics Forum | Wed Dec 17 14:39:18 EST 2003 | Dean
How do you know your profiler is correct? Do you have a pyrometer you can verif the PCB temp with?
Electronics Forum | Wed Dec 17 03:26:17 EST 2003 | Kev
Hi Lads, Thanks for all of the replies. To answer a few of your questions..... My wave is a Hollis PT500N. It has 3 zones of pre-heater rod elements. Each individual element (601195-01) is 500 watts. There are 16 elements per zone so 8 Kw per zone.
Electronics Forum | Thu Nov 04 11:56:33 EST 1999 | Tim Almy
Is 260 degrees C / 500 degrees F the optimum temperature for wave soldering ?
Electronics Forum | Mon Apr 16 12:59:51 EDT 2001 | Mike R
If you will place a temperature strip on the board during wave soldering process you will get a max of 210 F or 98.8 C which is normal on the standard wave temperature. The problem on the 10% solder on the TH via hole can be caused by insufficient fl
Electronics Forum | Sat Apr 14 03:25:04 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Sat Apr 14 03:25:10 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Thu Apr 05 12:27:12 EDT 2001 | davef
I concur with your second approach. A profile needs to be tailored to the design of the board, the components, and the solder paste. Your first approach seems to try to balance lower quality soldering with a lower process complexity.
Electronics Forum | Sat Apr 14 00:04:21 EDT 2001 | zam_bri
I'm not a Wave soldering guy and my friend have asked me a question on what is the best preheat time and temperature for Wave soldering.They experiences only 10% flow up thru the PTH barrel. I've asked them to increase the temperatue to 120 Deg C. Cu