Electronics Forum | Mon Nov 12 01:18:29 EST 2007 | sin4d
Hi, ALL I experience some QFP with wetting issue on the heel of the lead. There is no fillet wetting on the heel which causes reject bt the customer, but not all the QFP. Could anyone pls help what is the causes of this problem, it is due to oxidati
Electronics Forum | Tue Dec 18 18:36:58 EST 2001 | guicho_v
Is the Sn% of the plating of the pin related to wetting quality?. I am having issues with one IC maker where some pins are OK and one or two pins are not soldered, even when there is weeting evidence underneath the pin. I am blaming the %Sn too hig
Electronics Forum | Wed Sep 15 20:59:23 EDT 2010 | genesan
hi All, Here i snap shot previous PCB(HASL) and current PCB(Immersion Silver).Base on the photo it could be PCB oxidize cause the non wetting?
Electronics Forum | Mon Sep 13 22:32:41 EDT 2010 | genesan
Hi all good morning and need advice from expertise here. One of my customer complain that they have constantly issues with one of their product and ask us to do cross section.The report show there was “no wetting to the PCB copper pad” and cause the
Electronics Forum | Mon Sep 13 22:58:49 EDT 2010 | genesan
Hi all good morning and need advice from expertise here. One of my customer complain that they have constantly issues with one of their product and ask us to do cross section.The report show there was “no wetting to the PCB copper pad” and cause the
Electronics Forum | Tue Jul 30 17:47:50 EDT 2002 | davef
Dewetting: Solder does not adhere to lead or land, caused by: * Poor solderability of lands. * Poor solderability of leads. * Solder paste integrity. * Lead plating integrity. Need more information, please: * What is dewetting [ie, component, pad, e
Electronics Forum | Tue Sep 14 04:00:12 EDT 2010 | genesan
Hi Sir grahamcooper22, There should not a issue in stencil since i had open the aperature 1:1(one to one).Futhemore this is HASL pcb coating as now our customer had convert to immersion silver.I had do comparison between both and found HASL wetting n
Electronics Forum | Thu Dec 01 21:17:30 EST 2005 | davef
Does the solder melt when 'hit' with a soldering iron [and maybe a little flux]? If so, what is the appearance of the solder flow? What causes the green tint in the picture you provided?
Electronics Forum | Tue Jul 30 08:37:39 EDT 2002 | davef
When you talk about 'poor wetting', 'dewett', 'no wets', etc.; are you seeing solder pulling back or away from the pad? Please describe the condition. Dewetting. The condition in the solder joint in which the liquid solder has not adhered intimate
Electronics Forum | Fri Apr 09 20:47:36 EDT 2010 | 89jeong
I think the oxidation on the pad happens easily but do not on Au plated pad.The reason may be caused by improper cleaning or Au plating thickness in plating process. But,before suspecting the pcb board, you need to check your process or used material