No, none of us can tell you what is the acceptable level of halide content or contamination in flux residue. The level of harmful residues on your product helps determine the reliability of your product. We know nothing of your product, its custome
Electronics Forum | Fri Mar 14 11:04:54 EDT 2008 | herman
Samir, To correct some misconceptions on the answers to your question, and "what you know from experience": With both ENIG (Electroless Nickel/Immersion Gold-IAu) and IAg (immersion silver), soldering does not take place to the gold or the silver. Wh
Electronics Forum | Wed May 05 10:57:25 EDT 1999 | Kevin Hussey
| | | Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | | | | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | | | | | My question's are really : | |
Electronics Forum | Sun May 02 11:53:43 EDT 1999 | Chrys Shea
| | Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | | | My question's are really : | | how is the
Electronics Forum | Mon Feb 28 11:31:08 EST 2005 | russ
This sounds a lot like a profile that is killing flux activity prior to wave immersion. What is your topside preheat temp just prior to hitting the wave? What type of preheat do you have, convection or radiant? Are you using a chip/turbulent wave
Electronics Forum | Sun May 02 19:09:46 EDT 1999 | JohnW
| | | Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | | | | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | | | | | My question's are really : | |
Electronics Forum | Sat May 08 07:41:00 EDT 1999 | wayne sanita
hello, i have been using up-78 ultraprint for over a year now. at first we were getting lots of solder balls mainly on 0805's. this happened with all paste we used, too much solder under component leads. i have been using apertures reduced 10% homepl
Electronics Forum | Fri Oct 23 16:01:18 EDT 1998 | Earl Moon
| I need some info on how to stop the bridges I'm having on | radial and axial parts that are in the same place on every board. I'm also having problems with sot-25 bridging. I'm using a Electrovert E-pak. I tried leveling the machine,solder pot, an
Electronics Forum | Mon Oct 26 16:01:33 EST 1998 | tom Gervascio
| | I need some info on how to stop the bridges I'm having on | | radial and axial parts that are in the same place on every board. I'm also having problems with sot-25 bridging. I'm using a Electrovert E-pak. I tried leveling the machine,solder pot
Electronics Forum | Fri Jun 25 09:51:35 EDT 1999 | C.K.
| Dear John/Earl | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the Desired profilin