Electronics Forum | Sun Apr 05 18:59:15 EDT 1998 | Graham Naisbitt
Jaqueline There are so many variables in the electronic assembly manufacturing process involving more than 12 different chemistries, that it is impossible to easily identify and determine the nature and reason of such residues. GEC Hirst Research in
Electronics Forum | Mon Jan 26 11:46:16 EST 1998 | Rin Or
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Sun Jan 26 09:32:55 EST 2003 | davef
But soon after cleaning and drying with IPA, we find a white residue formation. A: IPA will not nothing to clean your board. The white residue is exactly what you should expect. Search the fine SMTnet Archives for background. >How do we avoid th
Electronics Forum | Sat Jan 25 20:17:40 EST 2003 | ramanandkini
We are soldering a 8 pin TTL chip on to a CEM1 board that has a hot air level soldering. We use no clean soler paste for the reflow process. Now the customer wants us to clean since he is afraid of flux attracting the dust. We have some SMT LEDs that
Electronics Forum | Mon Jan 27 12:02:00 EST 2003 | Mike Konrad
Dave is correct. No-clean flux + water = white residue (unless the proper chemical is mixed with the water). Additionally, no-clean flux + IPA = white residue. Many saponifiers work well as do other cleaning agents. White residue may also be a re
Electronics Forum | Mon Oct 30 21:43:08 EST 2006 | davef
So, after the repair of a BGA, you notice white reside on a nearby connector. Correct? [Sorry we're so dense. Long day.] Tell us about: * Flux class used in repair * Flux class used in original assembly Why are you baking the assembly after repair
Electronics Forum | Mon Oct 30 20:24:35 EST 2006 | davef
As we understand it, you: * Get some nice BGA from your supplier * Find BGA to be packaged properly * Bake the BGA for 24 hours at [what temperature?] to reduce the potntial for damaging moisture sensitive components during following processes * Remo
Electronics Forum | Fri Mar 02 15:52:19 EST 2001 | jagman
This happens to be after the water wash process. These are Burn-In boards so an SMT epoxy is used prior to wave. The flux used is Kester 2331ZX. Would using a thinner cause this to occur? The residue is all over the board. Thanks.
Electronics Forum | Fri Oct 13 05:21:08 EDT 2000 | Robert Steltman
Looking at the original post, it seems that the white residue is formed on the board after wave soldering and becomes evident when it has been left standing for a while. From what I understand, it seems that the solids content of the "no clean" flux
Electronics Forum | Fri Jun 19 15:17:54 EDT 1998 | Chris Jackson
We are in the process of validating Silicon 1C55 (thermal cure) conformal coating over Alpha LR725 solder paste. I am looking for anyone who may be using this process, or has been exposed to someone who is doing this process. Our concern is with the