Electronics Forum | Fri Jan 29 05:14:06 EST 1999 | Graham Naisbitt
Hi guys, I really am at a loss to understand this one. It would appear that there may be some reaction between the flux and the resist? Or maybe you have an OSP on the board that is reacting during soldering? As a fast fix, maybe you should try a
Electronics Forum | Wed Feb 10 12:52:21 EST 1999 | Dick Casagrande
|I'm getting in a little late on this but my 2 cents is: We have been using no-clean flux for a few years now but up till last month were still cleaning (the white residue) our boards (all thru hole). Finally did some investigation and found the flux
Electronics Forum | Mon Jul 01 00:09:47 EDT 2002 | Ben
Hi all How can I clean the white residue between QFP 0.5 mil Pitch? The white residue was created from mistake adding liquild No-clean flux Lonco 23F for reworking clean board. I can clean almost of it by using EC7M cleaning solvent except between
Electronics Forum | Mon Jul 01 20:44:17 EDT 2002 | davef
Actually, the white res were caused by the water carrier in your Lonco 23F reacting with the res from the nc flux used to solder the component in place. Comments are: * Some nc flux res are cleanable, some are not. Your supplier [Alpha?] can probab
Electronics Forum | Sun Apr 05 18:59:15 EDT 1998 | Graham Naisbitt
Jaqueline There are so many variables in the electronic assembly manufacturing process involving more than 12 different chemistries, that it is impossible to easily identify and determine the nature and reason of such residues. GEC Hirst Research in
Electronics Forum | Thu Apr 13 12:52:49 EDT 2006 | amol_kane
lint from what?...also roughly how often do you clean the oven? (not the heated chamber) but other areas to keep them clean? The operator say he has had to do it twice in 2 weeks to keep it clean due to the residue
Electronics Forum | Thu Apr 13 13:07:43 EDT 2006 | russ
lint from the factory conditions, enviromnent you know. We clean every 6 mos. you seem to be accumulating quite rapidly. unless you are cleaning at the first spec of this showing up
Electronics Forum | Mon Jan 19 20:25:52 EST 1998 | Steve Gregory
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Wed Jan 14 18:47:55 EST 1998 | Graham Naisbitt
Jerry This is the classic "White powder phenomenon" a little like the X files - loads of information but who do you trust? I know that GEC Hirst Research in the UK, identified over 16 different white powder residues so it is not an easy subject. Plea
Electronics Forum | Mon Jan 26 11:46:16 EST 1998 | Rin Or
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct