Electronics Forum | Thu Jan 28 08:58:10 EST 1999 | Peet
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe
Electronics Forum | Fri Jan 29 05:14:06 EST 1999 | Graham Naisbitt
Hi guys, I really am at a loss to understand this one. It would appear that there may be some reaction between the flux and the resist? Or maybe you have an OSP on the board that is reacting during soldering? As a fast fix, maybe you should try a
Electronics Forum | Wed Feb 10 12:52:21 EST 1999 | Dick Casagrande
|I'm getting in a little late on this but my 2 cents is: We have been using no-clean flux for a few years now but up till last month were still cleaning (the white residue) our boards (all thru hole). Finally did some investigation and found the flux
Electronics Forum | Sun Apr 05 18:59:15 EDT 1998 | Graham Naisbitt
Jaqueline There are so many variables in the electronic assembly manufacturing process involving more than 12 different chemistries, that it is impossible to easily identify and determine the nature and reason of such residues. GEC Hirst Research in
Electronics Forum | Sun Aug 29 19:17:34 EDT 2004 | aqueous
Chen, It is always best to place one�s effort on determining the cause and content of the residue rather than trying to work around it. The first thing you must determine is the nature of the residue. Is it flux? In many instances, the residue is
Electronics Forum | Fri Jul 23 14:41:41 EDT 2004 | Steve Stach
Dear JSK, It sounds like the root causes of your problem are two fold. First, excessive heat will polymerize the abietic acid found in rosin forming neo-abietic diamers and polymers which are much less soluble than the parent monomer. There are
Electronics Forum | Wed Jul 21 17:49:52 EDT 2004 | jsk
problem: Too many solvents and boards are not clean Flux remains on the board after vapor degreaser and "Powdery" white residue after vapor degreasing Flux type is kester 186 Process: hand solder High Temp alloy, spot clean after hand solder e
Electronics Forum | Fri Jan 15 10:52:27 EST 1999 | John
| Hi all, | | I thought I'd use this forum to ask a couple general questions on fluxes for manual operations: | First - Is it OK to use a wave soldering type flux (specifically OA)? Thinking about activation temperatures and the ramp rate of the wav
Electronics Forum | Fri Jan 15 03:30:10 EST 1999 | Jeff Sanchez
| Hi all, | | I thought I'd use this forum to ask a couple general questions on fluxes for manual operations: | First - Is it OK to use a wave soldering type flux (specifically OA)? Thinking about activation temperatures and the ramp rate of the wav
Electronics Forum | Thu Jan 14 16:32:58 EST 1999 | Dave Jurena
Hi all, I thought I'd use this forum to ask a couple general questions on fluxes for manual operations: First - Is it OK to use a wave soldering type flux (specifically OA)? Thinking about activation temperatures and the ramp rate of the wave solder