Electronics Forum | Wed Oct 11 10:29:28 EDT 2000 | G. English
Try the following steps : FIRST CHECK THE ARCHIVE for further information, it WILL help you. Step One : What�s the chemical analysis of this white res? Obtain a sample. It could be tin, rosin, or something else??? Step Two : The fastest way I know
Electronics Forum | Mon Jul 01 13:57:58 EDT 2013 | wpierowski
Recently on one product, I found a white residue on the solder joints only that is more of a gray in color. Our lab told us it was a tin oxide with an unknown organic. This is with a lead free OA paste and it only shows after wash. Has anyone seen
Electronics Forum | Thu Aug 06 09:51:20 EDT 1998 | Bob Willis
This text may be of interest to any one with tin lead spots Guide to Solder Spots - A New Plague in Manufacture ? So what are solder spots ? They appear to be the next big problem in modern reflow assembly in fact in any process that involves solder
Electronics Forum | Sat Jun 30 11:28:24 EDT 2001 | davef
Consider using a roll solder with a flux that well matches the residues you can accept to be remaining on the board when you get finished processing. Many people use a no-clean flux cored roll solder for such operations, because they don't want to c
Electronics Forum | Thu Mar 17 22:14:42 EST 2005 | Chua
Hi Davef, Thanks for your advise...... We are running no-clean process. If there is white residues after few days.....is it cause by those excess flux. Thanks
Electronics Forum | Tue May 19 12:54:55 EDT 1998 | Richard Jackson
| We had a similar problem. But whenever the solder came from the screen printer the solder would wet to the gold fingers, with the help of residual flux. But the problem is balls, that I assume are not wetted to the gold fingers but instead are jus
Electronics Forum | Mon May 18 21:29:38 EDT 1998 | D.Lange
| I've tried every thing I can think of. Do you have any | Ideas? | What I have is micro balls on the gold fingers of | panelize boards. These balls only appear on the gold | finger. Or at least I can only find them on the gold | fingers. | What I
Electronics Forum | Tue May 19 12:29:59 EDT 1998 | Richard Jackson
| Richard, | You may be encountering solder paste contamination | on the assembly during the printing process. Solder | will reflow on tin/lead plated lands therefore invisible. | If you are washing the assembly prior to inspection | then you are
Electronics Forum | Tue May 19 10:23:06 EDT 1998 | Mike C
| Howdy Richard, | Welcome to the club! I now dub thee a full fledged member of the "Spotty Gold Finger and Bleeding Ulcer Society"...or SGFBUS for short... (GRIN) | I know it's not funny to be in that position, but there's so many different places t
Electronics Forum | Fri Oct 08 02:31:07 EDT 1999 | Brian
| | | | Hi, | | | | | | | | Help! Could anyone help to enlighten me on this? | | | | | | | | Question: | | | | | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowab