Electronics Forum | Fri Apr 03 02:52:42 EST 1998 | Jacqueline Coia
At this moment in time we are using water soluble solder paste on our PCBs these are cleaned using water only, agitated with ultrasonics. After drying a white/grey residue is left around solder joints. Reflow profile is fine and a reliable wash proce
Electronics Forum | Wed Jan 27 21:02:53 EST 1999 | Dave F
| i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated temperatu
Electronics Forum | Thu Jan 28 08:58:10 EST 1999 | Peet
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe
Electronics Forum | Wed Jan 27 23:29:28 EST 1999 | parag palshikar
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe
Electronics Forum | Fri Jan 29 05:14:06 EST 1999 | Graham Naisbitt
Hi guys, I really am at a loss to understand this one. It would appear that there may be some reaction between the flux and the resist? Or maybe you have an OSP on the board that is reacting during soldering? As a fast fix, maybe you should try a
Electronics Forum | Wed Feb 10 12:52:21 EST 1999 | Dick Casagrande
|I'm getting in a little late on this but my 2 cents is: We have been using no-clean flux for a few years now but up till last month were still cleaning (the white residue) our boards (all thru hole). Finally did some investigation and found the flux
Electronics Forum | Fri Apr 03 08:22:36 EST 1998 | Scott Cook
| At this moment in time we are using water soluble solder paste on our PCBs these are cleaned using water only, agitated with ultrasonics. After drying a white/grey residue is left around solder joints. Reflow profile is fine and a reliable wash pro
Electronics Forum | Sun Apr 05 18:59:15 EDT 1998 | Graham Naisbitt
Jaqueline There are so many variables in the electronic assembly manufacturing process involving more than 12 different chemistries, that it is impossible to easily identify and determine the nature and reason of such residues. GEC Hirst Research in
Electronics Forum | Fri Apr 03 19:04:02 EST 1998 | Steve Gregory
Hi Jacqueline! The dreaded white residue huh? YUCK! This seems to be a ongoing issue...probably because there are many different things that can possibly cause this. There's a real good article about the different causes of this problem at Kest
Electronics Forum | Mon Jul 01 20:44:17 EDT 2002 | davef
Actually, the white res were caused by the water carrier in your Lonco 23F reacting with the res from the nc flux used to solder the component in place. Comments are: * Some nc flux res are cleanable, some are not. Your supplier [Alpha?] can probab