Electronics Forum | Mon Apr 29 09:54:46 EDT 2002 | davef
MadReindeer If this white residue is salt, * Why do you say is the presence of it 'not dangerous it only looking bad'? Don't salts sometimes go into solution with moisture on the board from humidity in the air and form cathodic plating shorts betw
Electronics Forum | Tue Sep 01 06:55:22 EDT 2009 | davef
Rocko: While you're rooting around with the cleaner to better understand the issues with your water supply, monitor the heaters of your cleaner. We've had instances were the heater control has created "white haze" problems. Are you sure the residue
Electronics Forum | Sun Feb 26 17:40:35 EST 2006 | GS
Hi, just my comment, theoretically No Clean means no Ion Contaminants from Flux, but it some some case ion contamination (Cl-Br-F) could come out from raw PCBs, from Components, from fingerprints, etc. To incorporate a ROSE step in the pro
Electronics Forum | Sun Feb 26 21:48:28 EST 2006 | Mike Konrad
Hi GS, Just a clarification� No-clean does NOT equal no ions. It equals less ions (at best). Automatic R.O.S.E (Resistivity Of Solvent Extract) testers are commonly used to detect ionic contamination from no-clean applications. Your comment rega
Electronics Forum | Mon Feb 27 17:08:15 EST 2006 | GS
3,5 ugr/cm2 NaCl) or power components, or Raw PCB. Nothing with the solder process or fluxes. Ion Chromatography analysis was necessary to help understanding of contamination origin. When occasionally we run TIC on a NC assembled PBA (Paste ROL0 or
Electronics Forum | Fri Sep 07 21:43:40 EDT 2001 | mugen
Hi, We use IPA and Prozone, if IPA is so drastically detrimental, to the pcba's.....what suggested alternative, can you please recommend, as IPA replacement? Thanks.
Electronics Forum | Thu Sep 06 10:55:37 EDT 2001 | davef
saturation occurs at ppm levels. Remember, IPA is extremely flammable and its bulk use makes the plant liable to all sorts of quite repressive safety rules/regulations and so on. Ignoring these rules exposes the owner to fines and possible plant cl
Electronics Forum | Wed Sep 05 14:53:45 EDT 2001 | Jeff Meier
We have customers that are requiring no flux residue left on boards after soldering of non-water washable parts. We currently use Multicore Crystal 502 No-Clean to solder parts that are not washable. Has anyone come up with a good way to remove this
Electronics Forum | Thu Sep 06 09:49:26 EDT 2001 | ksfacinelli
This is a real problem. We have experimented with a number of off the shelf products as well as discussed the issue with a few solder manufacturers. As you are aware IPA or Flux off can make the product look worse. I would discuss with the custome
Electronics Forum | Sun Jan 26 09:32:55 EST 2003 | davef
But soon after cleaning and drying with IPA, we find a white residue formation. A: IPA will not nothing to clean your board. The white residue is exactly what you should expect. Search the fine SMTnet Archives for background. >How do we avoid th