Electronics Forum | Fri Dec 16 13:31:03 EST 2005 | gpaelmo
Thanks for your response.
Electronics Forum | Fri Dec 16 13:31:28 EST 2005 | gpaelmo
Thanks for your response.
Electronics Forum | Fri Dec 16 08:16:41 EST 2005 | davef
Heat cycles deplete the pure tin layer. Each solder cycle reduces the tin thickness by ~0.1 micron (4 uin). So, if you start with a thin imm tin coating you'll have problems after multiple heat cycles. Steve Wentz says, "In almost every case I've
Electronics Forum | Fri Dec 16 03:47:46 EST 2005 | gpaelmo
Anyone have problems wave soldering white tin finish? We are an ems and our customer provides us the pcb's. SMT and TH components on the board. SMT is fine but when we wave solder, wetting to top side is very poor (solder only flows half way up). We
Electronics Forum | Fri Dec 16 08:00:26 EST 2005 | jax
What you are most likely dealing with: Insufficient Pure Sn layer ( multiple causes ) Because elevated temperatures accelerate the diffusion process, the thickness of the Pure Sn layer will reduce during every thermal cycle... ( bakeing PCBs, S
Electronics Forum | Thu Jan 15 15:13:50 EST 1998 | justin medernach
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Wed Jul 29 13:44:45 EDT 1998 | David Spilker
We are investigating alternatives to HASL finishes for more dense PWBs. OSP is not a good choice because of low solid flux and possibly long shelf life. Immersion gold is expensive and so far has been more difficult to wave solder. Has anyone had
Electronics Forum | Wed Aug 09 08:06:07 EDT 2006 | davef
See "IPC-4554 Specification for Immersion Tin Plating for Printed Circuit Boards" 3.2.1 Immersion Tin Thickness. The most common reason for solderability issues with the white tin surface coating during multiple thermal excursions is a thin white ti
Electronics Forum | Thu Dec 21 20:09:01 EST 2000 | Dave F
You are one lucky person to have access to the fine SMTnet Archives. They have over a hundred threads on immersion tin, white tin, and the other variants.
Electronics Forum | Tue Mar 01 08:21:37 EST 2005 | David Bratcher
What thickness is required to process a double sided board with white tin? Is there an IPC standard? If rework is necessary, what is required?