Electronics Forum | Thu Feb 15 18:35:10 EST 2024 | prestonames
Hi Mahmoud, I hope you were able to find a solution for your project! My company recently purchased an ASM Eagle Xtreme Gold Wire Bonder and we have been unable to locate the manual. Is it possible to share the manual that you have over email? Pleas
Electronics Forum | Fri Feb 16 15:12:27 EST 2024 | capse
ASMPT SEMI USA, Inc. 7850 S Hardy Drive, Suite 110, Tempe, AZ 85284-112 U.S.A. Phone: +1 602 437 4760
Electronics Forum | Tue Jul 18 16:49:49 EDT 2023 | mahasg
Hello All, I am PhD student at polytechnique Montreal. We have a CQFP44 packages and Dies of 51um pad pitch (22nm FDSOI tech) that I need to bond myself at the university using ASM Eagle Xtreme gold wire bonder in the university. we need to perform b
Electronics Forum | Tue Mar 01 15:42:16 EST 2016 | gregp
Bought a Machine from Tach Shebby at Fastex. It was on a skid at the customers facility ready to ship. I pay Fastex (wire transfer)...three weeks later the machine still hasn't shipped because he is trying to renegotiate his buy price with the owne
Electronics Forum | Mon May 07 15:13:03 EDT 2001 | jdtpfacreate
Singh, The equipment varies in price. We make a wire bonder called the HW27U-H Wire Bonder. This is a gold to gold wire ball bonder. The substrate size you mention is within the area we can take into the machine. The key is the bonding area.
Electronics Forum | Fri Jan 20 02:34:16 EST 2006 | yihui
Hi, i'm david, new to this forum. Came across your posting about using a delvotec bonder to TS bond to a ENIG pad. Given that the immersion gold layer is thin, does the capillary scrub through the gold layer to expose the underlying nickel? Does your
Electronics Forum | Thu Dec 29 03:57:16 EST 2005 | sparrow
Hello Chris, To be honest, it's hard to believe you could not bond to ENIG at all. Yes, the gold layer is thin and hard, but it just narrows the process window and does not make the bonding impossible. I say this, because we have been using TS gold w
Electronics Forum | Thu Dec 29 10:47:05 EST 2005 | Chris
The paper Dave posted the link for is great. I have to go back and read it in depth. I can build prototypes by wirebonding to ENIG. I can do it on a manual wirebonder but I don't have the patience to do it on a magazine to magazine automatic machi
Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu
Electronics Forum | Fri Aug 17 01:40:55 EDT 2001 | V.RAMANAND KINI
We are in the watch & clock Business. We have a Watch IC chip that has to be wirebonded using Ultrasonic aluminium wedge bonder. The wire dia is 1.25mil. The PCB is made of G10 Glass epoxy copper clad laminate. The copper thickness is 18 microns. The