Electronics Forum | Mon Mar 07 15:41:50 EST 2005 | John M
Is anyone aware of standards which would identify the clean room requirements for the wire bonding process ?
Electronics Forum | Mon Mar 07 21:37:42 EST 2005 | ABHI
It depends on your product requirements. I have seen aluminium wire bonding operations in as high as class 100K clean rooms. These are the assembly areas for calculators. The best is class 10K clean room for wire bonding. You can go upto fine pitch w
Electronics Forum | Thu Dec 29 10:47:05 EST 2005 | Chris
The paper Dave posted the link for is great. I have to go back and read it in depth. I can build prototypes by wirebonding to ENIG. I can do it on a manual wirebonder but I don't have the patience to do it on a magazine to magazine automatic machi
Electronics Forum | Tue Sep 10 10:42:36 EDT 2013 | capse
Plasma cleaning is used extensively to clean surfaces prior to wire bonding.
Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu
Electronics Forum | Fri Oct 06 04:23:06 EDT 2006 | David
What is the solder finish of the board?. If this is gold, maybe you should check the reflow profile and max temperature which can easely kill your gold coating so problems with bonding. Also we are using Prozone Multicore with ultrasonic to clean
Electronics Forum | Mon Sep 09 15:38:02 EDT 2013 | arendonk
Hi, We are having issues aluminum wirebonding on ENEPIG plated PCB by a too low pull force and or having lifts (1% range). Could any body advice how to solve this problem? Is there a special wire bond grade required? How to best clean contaminant
Electronics Forum | Thu Oct 05 07:23:34 EDT 2006 | Chris
Hi all experts, I have no background about PCB or SMT process. I am now encountering some issues after SMT - Unstable stitch bonding condition. I am now suspecting some contaminants remain on lead after cleaning. Therefore, how can I check th
Electronics Forum | Thu Oct 05 16:04:00 EDT 2006 | GS
I am not expert, just my comment, the total ionic contamination allowed after SMT, by using No Clean process, theoretically it should be close to Zero. Any way the Standard IPC-JSTD-001 allows 1,56 ugr NaCl/cm2 for the final Printed Board assembled.
Electronics Forum | Tue Jul 01 17:38:24 EDT 2003 | jartman
I've faced this several times in the past, and the only real solution is to wirebond before SMT assembly. Everything leaves a residue, and trying to clean a residue off later is basically hopeless. This may require some trickery in your SMT process