Electronics Forum | Mon Jun 03 16:21:11 EDT 2013 | stefgaudreau
Hi, I have a design were power supply multi strand wire (AWG18) are soldered directly on the pcb (thru-hole) by wave soldering process. I don't have any ferrule on the wire. I would like to know if the IPC standard allow this for class 3 assembly
Electronics Forum | Wed Jul 17 10:44:19 EDT 2013 | gregcr
Hi All, Has anyone seen or used equipment that is capable of automating the process of attaching hookup wire directly to a large SMT pad? Soldering, ultrasonic? I'm looking to see if there is a machine that is capable of automatically taking a tef
Electronics Forum | Thu Apr 03 12:36:30 EDT 2014 | jimmyboz
Hold the F1 key during power up, it will boot into the I/O screen. Check the 3 photo zones. Check the door switch. In the main screen you can cancel D1 or D2, then you can swap light sensors. Check carefully the wiring, there is a SYNC wire betwee
Electronics Forum | Sat Oct 08 11:57:58 EDT 2016 | davef
A friend in the contract coating business said: "... ask why the wire is [teflon] coated in the first place, as only the solder joints should be coated in this situation as the flexing/bending of the wires will cause the coating to crack and flake of
Electronics Forum | Wed Dec 14 20:17:48 EST 2016 | davef
As I understand, you are wire bond gold wire to gold pad, where the substrate has good bond strength, but the die does not. If bond quality is good, and then drops off rapidly, then it's probably something to do with contamination within the system
Electronics Forum | Mon Jun 26 08:57:17 EDT 2017 | capse
If N2 is not an option, the cut wire feeder or drilled wire are your best bet for now. You need to optimize wire feed rate as well. The solder joint on the robot takes about the same time to form as in manual soldering. If you need to speed the solde
Electronics Forum | Tue Nov 07 22:44:39 EST 2017 | wrander1
Hi I'm new to the world of wire bonding. I seem to have some sort of pad contamination Preventing gold wire from bonding to aluminum pats. There appears to be a dozen microns size particles. And a slight crackling of the surface at 500 X. I am send
Electronics Forum | Tue Feb 12 01:14:46 EST 2019 | sabeti
Hello Everybody, I have a problem with a DEK 265Lt, during downloading the vision, I get this error message: Vision hardware error Controlled lighting not responding FATAL ERROR - REINITIALISE MACHINE I have found that this might be due to a broke
Electronics Forum | Wed Apr 17 03:37:29 EDT 2019 | mahammansoor
Hi, I work in a Cable and Wire manufacturing company. We are currently working on an order of Automotive wires that require strict RoHS compliance. What are the RoHS compliance strategies that we can implement at the production line (PVC and Copper
Electronics Forum | Tue Nov 05 11:53:50 EST 2019 | markhoch
Does anyone have any experience trying to solder Anticapillary or Silicone Blocked (SBT) wire? It's designed to inhibit wicking of liquids and unfortunately that includes molten solder. We're experimenting with it for a potential high volume applicat