Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Electronics Forum | Wed Feb 21 14:14:11 EST 2007 | rgduval
Hi, Bill, Lead-free solder and paste manufacturers will be a great resource for you during the transition; they've tested their products extensively, and their application groups have been able to help me through the biggest changes. There are a fe
Electronics Forum | Thu Dec 11 09:15:06 EST 2014 | sreejhu
Hello Sir, Thanks for your reply. i just got a mail from the DIMA service group and they said the Oven setting is as follows: Max temp settings in each zone (Which is not the temperature on your product, but close to where the air flow comes out of
Electronics Forum | Mon Dec 22 18:10:44 EST 2014 | sreejhu
What do you mean by solder in ROHS. Can you please explain me little bit. Is that really important while doing lead free process. Also, please tell me wether a 8 zone (4 bottm and 4 top) reflow oven with 300 degree max.. Is good to do the lead free
Electronics Forum | Wed Dec 10 16:58:53 EST 2014 | sreejhu
Hello, yes you are absolutely correct. I agree with your point. Last week,I personally checked out my board on Heller 1088 which is a 8 zone reflow oven (4 on top and 4 on bottom) and the soldering came pretty nice. So comparing with that situation
Electronics Forum | Thu Dec 11 08:22:26 EST 2014 | emeto
The longer the oven, the better. You will have much more capabilities in creating the precise profiles the way you want them(with10-12 zone oven). I have worked with ovens from 2 to 12 zones and the difference is huge. In my opinion try to get a 10zo
Electronics Forum | Wed Dec 10 16:14:37 EST 2014 | jimpat
The 300 degrees is the temperature as measured at the sensor. The actual air temperature just above your PCB may actually be much less. If the oven is properly calibrated then the 300 should represent air temperature at the board but I have seen ma
Electronics Forum | Fri Dec 15 01:37:21 EST 2006 | shrikant_borkar
Hi, Hemendra Recently, We have carried out lead Free Soldering On our 4+1 Panasonic Reflow machine. Results were fine , but its Not Recommended for long Run. but the machine which you have is 5 zone machine and additional 2 cooling zone too. Check
Electronics Forum | Wed May 11 11:36:43 EDT 2005 | rlackey
Hi Peter, There is no Silver in it, which even in small quantities (0.3%-4%) improves solderability. I would try and see a demo on a similar machine to yours with a similar product as everyone can get their solder to look great in lab/showroom site
Electronics Forum | Fri Oct 29 09:45:08 EDT 2004 | pioneertechnology
In 1995 we bought 4 Vitronics U520 reflow ovens with top heat only. We ran these ovens until 2003 for both curing and lead reflow with no problems. In 1998 we bought 1 U520 top and bottom heat and one U820 top and bottom heat and once again we had