| https://www.eptac.com/soldertips/soldertips-gold-removal-and-wave-soldering-vs-hand-soldering/
SolderTips: Gold Removal and Wave Soldering vs Hand Soldering | EPTAC Skip to content Scroll Toll Free: 800.643.7822 Toggle navigation Training All Classes
| https://www.eptac.com/faqs/ask-helena-leo/ask/wet-sponge-cleaning-vs-dry-brass-sponge-cleaning
. This cracking allowed the tin to penetrate the plating on the tip, which prevented the tip from being tinned, thereby increasing the oxidation on the tip, rendering the tip useless and needing to be replaced
| https://www.eptac.com/soldertip/soldertips-gold-removal-and-wave-soldering-vs-hand-soldering/
SolderTips: Gold Removal and Wave Soldering vs Hand Soldering - EPTAC - Train. Work Smarter. Succeed Looking for solder training standards, manuals, kits, and more
| https://www.eptac.com/faqs/soldertips/soldertip/soldertips-gold-removal-and-wave-soldering-vs-hand-soldering
SolderTips: Gold Removal and Wave Soldering vs Hand Soldering - EPTAC - Train. Work Smarter. Succeed Looking for solder training standards, manuals, kits, and more
| https://www.eptac.com/soldertip/soldertips-solderability-issues-with-nickle-plated-surfaces/
: We are working with components with leads of tin/lead over nickel. After the manufacturing processes, some of the pins are exhibiting what appears to be flaking plating, leaving behind unsolderable surfaces
| https://www.eptac.com/soldertip/soldertips-dealing-with-the-problems-of-soldering-iron-tips-breaking-down/
. We are soldering lead free materials between 600 and 700 degrees F and increasing the contact dwell time by about 1 to 1.5 seconds. The new lead free alloys are high in tin content and the tin will dissolve the plating on the solder iron tip and eventually eat through the tip
. Read Answer Maximum Limits of Solder Bath Contamination Question: If we are using a solder pot to tin wires and create solder joints (splices
| https://www.eptac.com/faqs/soldertips?hsLang=en
: We are working with components with leads of tin/lead over nickel. After the manufacturing processes, some of the pins are exhibiting what appears to be flaking plating, leaving behind unsolderable surfaces
| https://www.eptac.com/faqs/soldertips
: We are working with components with leads of tin/lead over nickel. After the manufacturing processes, some of the pins are exhibiting what appears to be flaking plating, leaving behind unsolderable surfaces
.png)