Technical Library | 2019-07-02 23:02:05.0
The introduction of lead-free solders resulted in a selection of different chemistries for solder pastes. The higher melting points of lead-free alloys required thermal heat resistant rosin systems and activators that are active at elevated temperatures. As a result, more frequent maintenance of the filtration systems is required and machine downtime is increased.Last year a different method of cleaning reflow ovens was introduced. Instead of cooling down the process gasses to condensate the residues, a catalyst was used to maintain the clean oven. Catalytic thermal oxidation of residues in the nitrogen atmosphere resulted in cleaner heating zones. The residues were transformed into carbon dioxide. This remaining small amount of char was collected in the catalyst. In air ovens the catalyst was not seen as a beneficial option because the air extracted out of the oven was immediately exhausted into the environment. When a catalyst is used in an air environment there is not only the carbon dioxide residues, but also water. When a catalyst is used in an air reflow oven the question is where the water is going to. Will it condensate in the process part of the oven or is the gas temperature high enough to keep it out of the process area? A major benefit of using a catalyst to clean the air before it is exhausted into the environment is that the air pollution is reduced dramatically. This will make environmental engineers happy and result in less pollution of our nature. Apart from this, the exhaust tubes remain clean which reduces the maintenance of air ovens.This paper will give more detailed information of catalyst systems during development and performance in production lines.
Technical Library | 2023-09-08 06:33:02.0
Fume extraction starts with the capturing of airborne pollutants. In principle, the right collection strategy makes a decisive contribution to the quality of the extraction and filtration technology in air purification systems. Because the degree of collection is the basis for subsequent high-grade filtration, which ultimately results in the efficiency of an extraction system.
Technical Library | 2022-02-16 09:40:05.0
During the last couple of years, utilization of extraction and filtration systems has become standard in many manufacturing companies, in craft businesses as well as in laboratory and research facilities. Fume extraction systems clean the process air, but they should be applied in a targeted manner so that the best filtration performance can be guaranteed. Everything stands and falls with pollutant capturing, as only maximum particle capture will lead to maximum separation performance.
Technical Library | 2022-03-16 19:48:18.0
Dendrites, Electrochemical Migration (ECM) and parasitic leakage, are usually caused by process related contamination. For example, excess flux, poor handling, extraneous solder, fibers, to name a few. One does not normally relate these fails with environmental causes. However, creep corrosion is a mechanism by which electronic products fail in application, primarily related to sulfur pollution present in the air.1 The sulfur reacts with exposed silver, and to a lesser extent, exposed copper. This paper will explore various aspects of the creep corrosion chemical reaction
Technical Library | 2021-04-16 05:38:38.0
The overall process of manufacturing electronics assemblies is characterized by a number of very different procedures. Along the production chain, technologies for cutting, assembling, soldering, bonding, gluing, marking, potting, etc. are used, all of them have one thing in common: They produce airborne pollutants, some of which can have a significant impact on employees, manufacturing equipment and products - and for this reason need to be removed effectively and efficiently.
Technical Library | 2014-06-23 14:50:52.0
It was unusual to see chip terminations change colors when tin lead solders were used but with the introduction of lead free reflow soldering and the corresponding increases in reflow temperatures terminations are now changing colors. Two conditions are present when reflow temperatures are increased for lead free solder alloys that leads to discoloration. Reflow temperatures are above the melting point of tin (Sn MP is 232oC). Air temperatures commonly used in forced convection reflow systems are high enough to both melt the tin plating on the termination allowing it to be pulled into the solder joint due to solder joint liquid solder surface tension leaving behind the exposed nickel barrier. Now those metal oxide colors will be visible due to high air temperatures during reflow.
Technical Library | 2013-10-24 15:47:53.0
Reflow soldering in a nitrogen atmosphere is a common process consideration in surface mount technology assembly. This is because the use of nitrogen in reflow equipment may benefit the process as well as the quality of the end product, where it can increase the reliability of the solder joint. (...) The present study investigated thoroughly the effect of different reflow soldering atmosphere, which is air and nitrogen on IMC formation and growth
Technical Library | 2009-12-23 16:55:08.0
Leading up to the development of lead-free soldering alloys, Horizontal Convection* was developed for the reflow process. Getting the correct temperature profile, with the narrow process window in lead-free applications, is now more important than ever. In each chamber or zone, air is circulated toward one side of the oven above the PCB and toward the opposite side of the oven below the PCB, forming a cyclone around the board. The forced air circulation results in a uniform temperature profile along the entire circuit board assembly. This technology is ideal for the precise profiles needed for lead free soldering.
Technical Library | 2017-07-06 15:50:17.0
Head-in-pillow (HiP) is a BGA defect which happens when solder balls and paste can't contact well during reflow soldering. Package warpage was one of the major reasons for HiP formation. In this paper, package warpage was measured and simulated. It was found that the package warpage was sensitive to the thickness of inside chips. A FEM method considering viscoelastic property of mold compound was introduced to simulate package warpage. The CTE mismatch was found contributes to more than 90% of the package warpage value when reflowing at the peak temperature. A method was introduced to measure the warpage threshold, which is the smallest warpage value that may lead to HiP. The results in different atmospheres showed that the warpage threshold was 50μm larger in N2 than that in air, suggesting that under N2 atmosphere the process window for HiP defects was larger than that under air, which agreed with the experiments.
Technical Library | 2021-07-06 21:13:36.0
The surface finishes commonly used on printed circuit boards (PCBs) have an effect on solder paste performance in the surface mount process. Some surface finishes are non-planar like hot air solder level (HASL) which can lead to inconsistencies in solder paste printing. Other surface finishes are difficult to wet during reflow like organic solderability preservative (OSP). What is the overall effect of surface finish on solder paste performance? Which solder paste is best for each surface finish? It is the goal of this paper to answer these questions.