Technical Library | 2022-09-25 20:03:37.0
Cracking remains the major reason of failures in multilayer ceramic capacitors (MLCCs) used in space electronics. Due to a tight quality control of space-grade components, the probability that as manufactured capacitors have cracks is relatively low, and cracking is often occurs during assembly, handling and the following testing of the systems. Majority of capacitors with cracks are revealed during the integration and testing period, but although extremely rarely, defective parts remain undetected and result in failures during the mission. Manual soldering and rework that are often used during low volume production of circuit boards for space aggravate this situation. Although failures of MLCCs are often attributed to the post-manufacturing stresses, in many cases they are due to a combination of certain deviations in the manufacturing processes that result in hidden defects in the parts and excessive stresses during assembly and use. This report gives an overview of design, manufacturing and testing processes of MLCCs focusing on elements related to cracking problems. The existing and new screening and qualification procedures and techniques are briefly described and assessed by their effectiveness in revealing cracks. The capability of different test methods to simulate stresses resulting in cracking, mechanisms of failures in capacitors with cracks, and possible methods of selecting capacitors the most robust to manual soldering stresses are discussed.
Technical Library | 2008-10-23 15:36:58.0
As part of continuous process improvement at KEMET, most failure modes caused by the capacitor manufacturing process have been systematically eliminated. Today these capacitor manufacturing-related defects are now at a parts per billion (PPB) level. Pareto analysis of customer complaints indicates that the #1 failure mode is IR failure due to flex cracks.
Technical Library | 2019-08-15 13:31:52.0
Cracks in ceramic chip capacitors can be introduced at any process step during surface mount assembly. Thermal shock has become a "pat" answer for all of these cracks, but about 75 to 80% originate from other sources. These sources include pick and place machine centering jaws, vacuum pick up bit, board depanelization, unwarping boards after soldering, test fixtures, connector insulation, final assembly, as well as defective components. Each source has a unique signature in the type of crack that it develops so that each can be identified as the source of error.
Technical Library | 2023-11-27 18:19:40.0
This page introduces major causes and countermeasures of solder crack in MLCCs (Multilayer Ceramic Chip Capacitors). Major causes of solder cracks Solder cracks on MLCCs developed from severe usage conditions after going on the market and during manufacturing processes such as soldering. Applications and boards that specially require solder crack countermeasures Solder cracks occur mainly because of thermal fatigue due to thermal shock or temperature cycles or the use of lead-free solder, which is hard and fragile.
Technical Library | 2009-05-21 13:41:05.0
Failure due to board flex cracks persists as the dominant failure mode in multi-layer ceramic capacitors (MLCC). (...) This paper is intended to show the impact of temperature cycling, high-temperature life tests, and multiple bend exposures to the MLCC with this flexible termination.
Technical Library | 2015-12-23 16:57:27.0
The onset of copper barrel cracks is typically induced by the presence of manufacturing defects. In the absence of discernible manufacturing defects, the causes of copper barrel cracks in printed circuit board (PCB) plated through holes is not well understood. Accordingly, there is a need to determine what affects the onset of barrel cracks and then control those causes to mitigate their initiation.The objective of this research is to conduct a design of experiment (DOE) to determine if there is a relationship between PCB fabrication processes and the prevalence of fine barrel cracks. The test vehicle used will be a 16-layer epoxy-based PCB that has two different sized plated through holes as well as buried vias.
Technical Library | 2009-10-08 01:58:04.0
In the present study, we report novel ferroelectric-epoxy based polymer nanocomposites that have the potential to surpass conventional composites to produce thin film capacitors over large surface areas, having high capacitance density and low loss. Specifically, novel crack resistant and easy to handle Resin Coated Copper Capacitive (RC3) nanocomposites capable of providing bulk decoupling capacitance for a conventional power-power core, or for a three layer Voltage-Ground-Voltage type power core, is described.
Technical Library | 2017-06-22 17:11:53.0
C-mode scanning acoustic microscopy (C-SAM) is a non-destructive inspection technique showing the internal features of a specimen by ultrasound. The C-SAM is the preferred method for finding “air gaps” such as delamination, cracks, voids, and porosity. This paper presents evaluations performed on various advanced packages/assemblies especially flip-chip die version of ball grid array/column grid array (BGA/CGA) using C-SAM equipment. For comparison, representative x-ray images of the assemblies were also gathered to show key defect detection features of the two non-destructive techniques.
Technical Library | 2019-04-07 22:47:46.0
How to protect your PCB from moisture related damage? J-STD-033 put forward stricter regulation on the MSD exposure environment,when the exposure time exceed the tolerated,the moisture will penetrate into electronics,Moreover, the newest RoHS regulation will rise soldering temperature,the sudden high temperature will lead to expansion and cracking on electronic components. In order to decrease the moisture defect on PCB for the manufacturers in China,Climatest Symor® begin to concentrated on electronic dry cabinet R&D since early 1990s,we specialize in handling temperature and humidity for 20 years,and we provide best solution for PCB storage.
Technical Library | 2017-08-31 13:43:48.0
Wire bonded packages using conventional copper leadframe have been used in industry for quite some time. The growth of portable and wireless products is driving the miniaturization of packages resulting in the development of many types of thin form factor packages and cost effective assembly processes. Proper optimization of wire bond parameters and machine settings are essential for good yields. Wire bond process can generate a variety of defects such as lifted bond, cracked metallization, poor intermetallic etc. NSOP – non-stick on pad is a defect in wire bonding which can affect front end assembly yields. In this condition, the imprint of the bond is left on the bond pad without the wire being attached. NSOP failures are costly as the entire device is rejected if there is one such failure on any bond pad. The paper presents some of the failure modes observed and the efforts to address NSOP reduction