Technical Library | 2022-09-25 20:18:33.0
Printed circuit board (PCB) bending and/or flexing is an unavoidable phenomenon that is known to exist and is easily encountered during electronic board assembly processes. PCB bending and/or flexing is the fundamental source of tensile stress induced on the electronic components on the board assembly. For more brittle components, like ceramic-based electronic components, micro-cracks can be induced, which can eventually lead to a fatal failure of the components. For this reason, many standards organizations throughout the world specify the methods under which electronic board assemblies must be tested to ensure their robustness, sometimes as a pre-condition to more rigorous environmental tests such as thermal cycling or thermal shock.
Technical Library | 2022-09-25 20:03:37.0
Cracking remains the major reason of failures in multilayer ceramic capacitors (MLCCs) used in space electronics. Due to a tight quality control of space-grade components, the probability that as manufactured capacitors have cracks is relatively low, and cracking is often occurs during assembly, handling and the following testing of the systems. Majority of capacitors with cracks are revealed during the integration and testing period, but although extremely rarely, defective parts remain undetected and result in failures during the mission. Manual soldering and rework that are often used during low volume production of circuit boards for space aggravate this situation. Although failures of MLCCs are often attributed to the post-manufacturing stresses, in many cases they are due to a combination of certain deviations in the manufacturing processes that result in hidden defects in the parts and excessive stresses during assembly and use. This report gives an overview of design, manufacturing and testing processes of MLCCs focusing on elements related to cracking problems. The existing and new screening and qualification procedures and techniques are briefly described and assessed by their effectiveness in revealing cracks. The capability of different test methods to simulate stresses resulting in cracking, mechanisms of failures in capacitors with cracks, and possible methods of selecting capacitors the most robust to manual soldering stresses are discussed.
Technical Library | 2019-08-15 13:31:52.0
Cracks in ceramic chip capacitors can be introduced at any process step during surface mount assembly. Thermal shock has become a "pat" answer for all of these cracks, but about 75 to 80% originate from other sources. These sources include pick and place machine centering jaws, vacuum pick up bit, board depanelization, unwarping boards after soldering, test fixtures, connector insulation, final assembly, as well as defective components. Each source has a unique signature in the type of crack that it develops so that each can be identified as the source of error.
Technical Library | 2019-08-14 08:27:46.0
There are five forms of carrier tape sealing cracking. In particular, it is more important to seal products such as IC components (IC tape carriers) and lighter and thinner LED components (LED tape carriers).
Technical Library | 2019-04-07 22:47:46.0
How to protect your PCB from moisture related damage? J-STD-033 put forward stricter regulation on the MSD exposure environment,when the exposure time exceed the tolerated,the moisture will penetrate into electronics,Moreover, the newest RoHS regulation will rise soldering temperature,the sudden high temperature will lead to expansion and cracking on electronic components. In order to decrease the moisture defect on PCB for the manufacturers in China,Climatest Symor® begin to concentrated on electronic dry cabinet R&D since early 1990s,we specialize in handling temperature and humidity for 20 years,and we provide best solution for PCB storage.
Technical Library | 2020-09-30 19:23:47.0
There is an increase in the number of optical sensors and cameras being integrated into electronics devices. These go beyond cell phone cameras into automotive sensors, wearables, and other smart devices. The applications can be lens bonding, waveguide imprinting, or other applications where the adhesive is in the optical pathway. To support these various optical applications, new materials with tailorable optical properties are required. There is often a mismatched refractive index between plastic lenses such as PC (Poly Carbonate), COP (Cyclo Olefin Polymer), COC (Cyclo Olefin Copolymer), PMMA (Poly Methyl Methacrylate), and UV curable liquid adhesive. A UV curable liquid adhesive is needed where you can alter the refractive index from 1.470 to 1.730, and maintain high optical performance as yellowness index, haze, and transmittance. This wide range of refractive index possibilities provides optimized optical design. Using particular plastic lens must consider how chemical attack is occurring during the process. Another consideration is that before the UV curable liquid adhesive is cured, chemical raw component can attack the plastic lens which then cracks and delaminates. We will also show engineering and reliability data which defined root cause and provided how optical performance is maintained under different reliability conditions.
Technical Library | 2019-04-11 05:59:57.0
Are your MSD safely stored? As humidity is found to be one of the key reasons for rejected products, many manufacturers are taking measures to control the humidity to increase their production efficiency and save the cost. In the industries of semi-conductor and electronics, the key section in which the rejected products are most probably to be made is that during the heating process of SMT, the IC(e.g.,PBGA,BGA,or TQFD) is likely to crack and thus cause non-effective welding because of the humidity. Climatest Symor® auto dry cabinet is the best solution to avoid the cracking and non#2;effective welding by dehumidifying the surface of your components. The dry unit can be used for 20 years without replacement,and controller is calibration free within 5 years.We attach dry cabinet application with different humidity range,welcome to download.
Technical Library | 2014-10-30 01:48:43.0
The ultimate life of a microelectronics component is often limited by failure of a solder joint due to crack growth through the laminate under a contact pad (cratering), through the intermetallic bond to the pad, or through the solder itself. Whatever the failure mode proper assessments or even relative comparisons of life in service are not possible based on accelerated testing with fixed amplitudes, or random vibration testing, alone. Effects of thermal cycling enhanced precipitate coarsening on the deformation properties can be accounted for by microstructurally adaptive constitutive relations, but separate effects on the rate of recrystallization lead to a break-down in common damage accumulation laws such as Miner's rule. Isothermal cycling of individual solder joints revealed additional effects of amplitude variations on the deformation properties that cannot currently be accounted for directly. We propose a practical modification to Miner's rule for solder failure to circumvent this problem. Testing of individual solder pads, eliminating effects of the solder properties, still showed variations in cycling amplitude to systematically reduce subsequent acceleration factors for solder pad cratering. General trends, anticipated consequences and remaining research needs are discussed
Technical Library | 2019-11-15 02:20:26.0
Material Aging Test-UV Weathering Test Chamber 1.What is UV aging? UV aging chambers use fluorescent ultraviolet lamp as light source to simulate UV radiation and condensation in natural sunlight, and to carry out accelerated weather resistance test in order to obtain the result of weather resistance of the material. UV aging detection is widely used in non-metallic materials, organic materials (such as coatings, paints, rubber, plastics and their products) under the change of sunlight, humidity, temperature, condensation and other climatic conditions to test the aging degree and situation of related products and materials. 2.Why we should do UV aging test? When the product is placed in the ambient environment, there will be different problems taken place, such as appearance changes, including cracking, speckle, powdering or color change, and even performance degradation,which may be due to the loss of components in the resin resulting in chemical bonds changes inside the molecular structure, this is mainly caused by sunlight, industrial exclusion of waste gas, bacteria and so on. The aging performance of the product directly affects the lifespan of the product, so aging test become significant,non-metallic materials, organic materials (such as paints, paints, rubber, plastics and their products) are subject to changes in sunlight, humidity, temperature, condensation and other climatic conditions to test the degree and condition of aging of related products and materials. The natural aging test is to put the plastic specimen under the sun exposure, and it is directly under the natural climate environment,to test the material performance under various factors such as light, heat energy, atmospheric humidity, oxygen and ozone, industrial pollution and the like, the most harsh climate condition should be selected,or near the actual application area of the material, the test site shall be open and flat, no obstacle to affect the test results,the specimen holder shall be facing the equator and at an angle of 45 ° from the ground. When the main performance index of the specimen has been reduced, the test s/b terminated when it achieve the minimum allowable use value . in most case,the test is terminated when the product primary performance index falls to 50% of the initial value. The natural aging process is a very slow process, and there is a great difference in different geographical conditions, which brings difficulties to evaluate the aging resistance of the product. It is an attempt to make an evaluation of the aging performance of the plastic in a shorter time,that is accelerated aging test. The accelerated aging test can be used to simulate the human light source of the fluorescent lamp, including the carbon arc lamp, the xenon arc lamp and the fluorescent ultraviolet lamp, and the artificial light sources can generate more light than the natural sunlight on the ground. When these artificial light sources are used, it is also common to use the combination of the condenser to simulate the rain drop, the dew and the like to conduct the aging test on the product.