Technical Library | 2008-10-29 18:45:53.0
Growing demand for compact, multi-function electronics products has accelerated component miniaturization and high-density placement, creating new challenges for the electronics manufacturing industry. It is no longer adequate to simply place parts accurately per a pre-defined CAD assembly program because solder paste alignment errors are increasing for numerous reasons. The solution to this problem is a system in which the placement machine can automatically detect and compensate for misalignment of the solder paste to produce high-quality boards regardless of the process errors beforehand.
Technical Library | 2020-07-02 01:14:44.0
Head-in-Pillow (HIP) defects are a growing concern in the electronics industry. These defects are usually believed to be the result of several factors, individually or in combination. Some of the major contributing factors include: surface quality of the BGA spheres, activity of the paste flux, improper placement / misalignment of the components, a non-optimal reflow profile, and warpage of the components. To understand the role of each of these factors in producing head-in-pillow defects and to find ways to mitigate them, we have developed two in-house tests.
Technical Library | 2013-03-12 13:25:18.0
High density and miniaturized circuit assemblies challenge the solder paste printing process. The use of small components such as 0201, 01005 and μBGA devices require good paste release to prevent solder paste bridging and misalignment. When placing these miniaturized components, taller paste deposits are often required. To improve solder paste deposition, a nano-coating is applied to laser cut stencils to improve transfer efficiency. One concern is the compatibility of the nano-coating with cleaning agents used in understencil wipe and stencil cleaning. The purpose of this research is to test the chemical compatibility of common cleaning agents used in understencil wipe and stencil cleaning processes.Compatibility of Cleaning Agents With Nano-Coated Stencils
Technical Library | 1999-05-06 12:08:08.0
Input voltage capacitors are typically the parts that fail first in a high power circuit. Today's requirements for increasingly smaller packages is driving high component densities in power systems, as in all systems. As the package size...
Technical Library | 2012-12-26 14:18:24.0
Passive components including resistors, capacitors, inductors, and circuit-protection devices compose the highest percentage of all devices that are populated on today’s PCB assemblies. However, the successful isolation and testing of these components during ICT is perhaps the most challenging and the least understood of all modern-day validation practices.
Technical Library | 2022-09-25 20:03:37.0
Cracking remains the major reason of failures in multilayer ceramic capacitors (MLCCs) used in space electronics. Due to a tight quality control of space-grade components, the probability that as manufactured capacitors have cracks is relatively low, and cracking is often occurs during assembly, handling and the following testing of the systems. Majority of capacitors with cracks are revealed during the integration and testing period, but although extremely rarely, defective parts remain undetected and result in failures during the mission. Manual soldering and rework that are often used during low volume production of circuit boards for space aggravate this situation. Although failures of MLCCs are often attributed to the post-manufacturing stresses, in many cases they are due to a combination of certain deviations in the manufacturing processes that result in hidden defects in the parts and excessive stresses during assembly and use. This report gives an overview of design, manufacturing and testing processes of MLCCs focusing on elements related to cracking problems. The existing and new screening and qualification procedures and techniques are briefly described and assessed by their effectiveness in revealing cracks. The capability of different test methods to simulate stresses resulting in cracking, mechanisms of failures in capacitors with cracks, and possible methods of selecting capacitors the most robust to manual soldering stresses are discussed.
Technical Library | 1999-05-09 12:51:38.0
This Technical Note outlines, step by step, the easiest ways to remove and replace surface mounted devices, using the lowest possible temperatures. This document discusses the following topics: Removal and replacement of discrete and passive components (capacitors, resistors, SOTs), Removal of two-sided components (SOICs, SOJs, TSOPs), Removal of quad components (PLCCs, QFPs), Replacement of quad components including fine-pitched devices.
Technical Library | 2011-07-07 03:37:13.0
The demand for miniaturized electronic equipment and fully-automated assembly lines for mass-production of new products require the availability of a complete range of SMD components
Technical Library | 2018-12-05 14:52:23.0
The multilayer ceramic capacitor (MLCC) has become a widely used electronics component both for surface mount and embedded PCB applications. The MLCC technologies have gone through a number of material and process changes such as the shift from precious metal electrode (PME) configurations which were predominantly silver/palladium to base metal electrodes (BME) dominated by nickel. Each of these changes were accompanied by both quality and reliability problems. The MLCC industry is now in the midst of an unprecedented set of challenges similar to the Moore’s Law challenges being faced by the semiconductor industry. While capacitor failures have historically been responsible for a significant percentage of product field failures (most estimates are ~30%) we are seeing disturbing developments in the low voltage (
Technical Library | 2019-08-15 13:31:52.0
Cracks in ceramic chip capacitors can be introduced at any process step during surface mount assembly. Thermal shock has become a "pat" answer for all of these cracks, but about 75 to 80% originate from other sources. These sources include pick and place machine centering jaws, vacuum pick up bit, board depanelization, unwarping boards after soldering, test fixtures, connector insulation, final assembly, as well as defective components. Each source has a unique signature in the type of crack that it develops so that each can be identified as the source of error.
winsouce.jpg)