Technical Library | 2015-08-20 15:51:08.0
Temperature and Humidity on Selective Conformal Coating It is well known that selective conformal coating on printed circuit board (PCB) assemblies provides unparallel protection for PCB’s. Nevertheless, concentrated conditions of humidity, water, and high temperatures can have negative effects on the conformal coating itself causing it to fail and become inapt for its intended purpose. Taking this into consideration, it is prudent to choose the right type of conformal coating that best suits the application and environmental conditions under which an assembly is likely to undergo in use. The proper conformal coating will significantly reduce the likelihood of failure/rejection, saving both valuable time and money for any manufacturing process.
Technical Library | 2015-07-27 16:58:29.0
When it comes to the application of conformal coating, curing the coating plays a key role in the circuit assembly and selective conformal coating process. Curing conformal coating occurs after the coating spray/dispense process is complete. The coating is considered “cured” when the conformal coating on the circuit assembly is sufficiently tack-free to be handled. Curing can sometimes be accomplished at room temperature but takes a considerable amount of time to dry. Accelerated conformal coating curing decreases this drying period, the cure process reaches either the tack-free or a fully dried state but not quite having fully cured properties. Accelerated curing techniques include one or a combination of heat, moisture, UV light, and chemical reaction curing. This article focuses primarily on thermal or heat curing.
Technical Library | 2022-01-26 15:22:33.0
Reliability of conformal coatings used to mitigate tin whisker growth depends on their ability to contain tin whiskers. Two key material properties required to assess the reliability of a polyurethane coating are documented experimentally: adhesion strength and puncture strength. A modified blister test using a predefined blister area is employed to assess the adhesion strength and a puncture test is employed to evaluate the puncture strength of the coating. After measuring the properties at time zero, the coatings are subjected to accelerated testing conditions (high temperature/humidity storage and temperature cycling) and the degradations of the coating properties are documented.
Technical Library | 2021-08-11 01:00:37.0
Conformal coatings and potting materials continue to create issues for the electronics industry. This webinar will dig deeper into the failure modes of these materials, specifically issues with Coefficient of Thermal Expansion (CTE), delamination, cracking, de-wetting, pinholes/bubbles and orange peel issues with conformal coatings and what mitigation techniques are available. Similarly, this webinar will look at the failure modes of potting materials, (e.g Glass Transition Temperature (Tg), PCB warpage, the effects of improper curing and potential methods for correcting these situations.
Technical Library | 2020-01-01 17:06:52.0
The majority of electronic failures occur due to thermally induced stresses and strains caused by excessive differences in coefficients of thermal expansion (CTE) across materials.CTE mismatches occur in both 1st and 2nd level interconnects in electronics assemblies. 1st level interconnects connect the die to a substrate. This substrate can be underfilled so there are both global and local CTE mismatches to consider. 2nd level interconnects connect the substrate, or package, to the printed circuit board (PCB). This would be considered a "board level" CTE mismatch. Several stress and strain mitigation techniques exist including the use of conformal coating.
| 1 |