Technical Library | 2013-08-22 14:28:58.0
Tin-rich solders are widely applied in the electronic industry in the majority of modern printed circuit boards (PCBs). Because the use of lead-tin solders has been banned in the European Union since 2006, the problem of the bridging of adjacent conductors due to tin whisker growth (limited before by the addition of Pb) has been reborn. In this study tin alloys soldered on glass-epoxy laminate (typically used for PCBs) are considered. Scanning ion microscopy with Focused Ion Beam (FIB) system and energy-dispersive X-ray spectroscopy (EDXS) were used to determine correlations between spatial non-uniformities of the glass-epoxy laminate, the distribution of intermetallic compounds and whisker growth.
Technical Library | 2018-04-18 23:55:01.0
Higher functionality, higher performance and higher reliability with smaller real estate are the mantras of any electronic device and the future guarantees more of the same. In order to achieve the requirements of these devices, designs must incorporate fine line and via pitch while maintain good circuitry adhesion at a smooth plating-resin interface to improve signal integrity. The Semi-Additive Process (SAP) is a production-proven method used on low dielectric loss tangent (Df) build-up materials that enables the manufacture of ultra-fine circuitry. (...) This paper will discuss a new SAP process for low loss build-up materials with low desmear roughness (Ra= 40-100 nm) and excellent adhesion (610-680 gf/cm) at various processing conditions. Along with the process flow, the current work will also present results and a discussion regarding characterization on the morphology and composition of resin and/or metal plating surfaces using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX), surface roughness analysis, plating-resin adhesion evaluation from 90o peel tests
Technical Library | 2021-11-03 17:05:39.0
Additively printed circuits provide advantages in reduced waste, rapid prototyping, and versatile flexible substrate choices relative to conventional circuit printing. Copper (Cu) based inks along with intense pulsed light (IPL) sintering can be used in additive circuit printing. However, IPL sintered Cu typically suffer from poor solderability due to high roughness and porosity. To address this, hybrid Cu ink which consists of Cu precursor/nanoparticle was formulated to seed Cu species and fill voids in the sintered structure. Nickel (Ni) electroplating was utilized to further improve surface solderability. Simulations were performed at various electroplating conditions and Cu cathode surface roughness using the multi-physics finite element method. By utilizing a mask during IPL sintering, conductivity was induced in exposed regions; this was utilized to achieve selective Ni-electroplating. Surface morphology and cross section analysis of the electrodes were observed through scanning electron microscopy and a 3D optical profilometer. Energy dispersive X-ray spectroscopy analysis was conducted to investigate changes in surface compositions. ASTM D3359 adhesion testing was performed to examine the adhesion between the electrode and substrate. Solder-electrode shear tests were investigated with a tensile tester to observe the shear strength between solder and electrodes. By utilizing Cu precursors and novel multifaceted approach of IPL sintering, a robust and solderable Ni electroplated conductive Cu printed electrode was achieved.
| 1 |