Technical Library | 2024-09-02 21:02:46.0
In conformal coating, there are several mechanisms that cause failure of printed circuit boards (PCBs). In a series of technical bulletins SCH will examine the common failure mechanisms in conformal coating including capillary flow, delamination, cracking, loss of adhesion, dewetting, corrosion, orange peel, pinholes, bubbles and foam.
Technical Library | 2008-12-11 01:15:56.0
Flame retardants have been around since the Egyptians and Romans used alum to reduce the flammability of wood. Brominated flame retardants (BFRs) first experienced use after World War II as the substitution of wood and metal for plastics and foams resulted in materials that were much more flammable. The widespread use of BFRs initiated in the 1970s with the explosion of electronics and electrical equipment and housings. For the US market, all of these products must conform to the UL 94 flammability testing specifications. In fact, the most common printed circuit board (PCB) in the electronics industry, FR-4, is defined by its structure (glass fiber in an epoxy matrix) and its compliance to UL 94 V0 standard.
Technical Library | 2020-08-27 01:22:45.0
Initially adopted internal specifications for acceptance of printed circuit boards (PCBs) used for wire bonding was that there were no nodules or scratches allowed on the wirebond pads when inspected under 20X magnification. The nodules and scratches were not defined by measurable dimensions and were considered to be unacceptable if there was any sign of a visual blemish on wire-bondable features. Analysis of the yield at a PCB manufacturer monitored monthly for over two years indicated that the target yield could not be achieved, and the main reasons for yield loss were due to nodules and scratches on the wirebonding pads. The PCB manufacturer attempted to eliminate nodules and scratches. First, a light-scrubbing step was added after electroless copper plating to remove any co-deposited fine particles that acted as a seed for nodules at the time of copper plating. Then, the electrolytic copper plating tank was emptied, fully cleaned, and filtered to eliminate the possibility of co-deposited particles in the electroplating process. Both actions greatly reduced the density of the nodules but did not fully eliminate them. Even though there was only one nodule on any wire-bonding pad, the board was still considered a reject. To reduce scratches on wirebonding pads, the PCB manufacturer utilized foam trays after routing the boards so that they did not make direct contact with other boards. This action significantly reduced the scratches on wire-bonding pads, even though some isolated scratches still appeared from time to time, which caused the boards to be rejected. Even with these significant improvements, the target yield remained unachievable. Another approach was then taken to consider if wire bonding could be successfully performed over nodules and scratches and if there was a dimensional threshold where wire bonding could be successful. A gold ball bonding process called either stand-off-stitch bonding (SSB) or ball-stitch-on-ball bonding (BSOB) was used to determine the effects of nodules and scratches on wire bonds. The dimension of nodules, including height, and the size of scratches, including width, were measured before wire bonding. Wire bonding was then performed directly on various sizes of nodules and scratches on the bonding pad, and the evaluation of wire bonds was conducted using wire pull tests before and after reliability testing. Based on the results of the wire-bonding evaluation, the internal specification for nodules and scratches for wirebondable PCBs was modified to allow nodules and scratches with a certain height and a width limitation compared to initially adopted internal specifications of no nodules and no scratches. Such an approach resulted in improved yield at the PCB manufacturer.
| 1 |