Technical Library | 2013-12-27 10:39:21.0
The head-in-pillow defect has become a relatively common failure mode in the industry since the implementation of Pb-free technologies, generating much concern. A head-in-pillow defect is the incomplete wetting of the entire solder joint of a Ball-Grid Array (BGA), Chip-Scale Package (CSP), or even a Package-On-Package (PoP) and is characterized as a process anomaly, where the solder paste and BGA ball both reflow but do not coalesce. When looking at a cross-section, it actually looks like a head has pressed into a soft pillow. There are two main sources of head-in-pillow defects: poor wetting and PWB or package warpage. Poor wetting can result from a variety of sources, such as solder ball oxidation, an inappropriate thermal reflow profile or poor fluxing action. This paper addresses the three sources or contributing issues (supply, process & material) of the head-in-pillow defects. It will thoroughly review these three issues and how they relate to result in head-in pillow defects. In addition, a head-in-pillow elimination plan will be presented with real life examples will be to illustrate these head-in-pillow solutions.
Technical Library | 1999-04-26 11:52:34.0
An evaluation of two fluxers, one with a reciprocating ultrasonic head and the other with microjets, was performed using nine independent criteria. The paper describes the methods of testing and the results.
Technical Library | 2008-10-29 18:45:53.0
Growing demand for compact, multi-function electronics products has accelerated component miniaturization and high-density placement, creating new challenges for the electronics manufacturing industry. It is no longer adequate to simply place parts accurately per a pre-defined CAD assembly program because solder paste alignment errors are increasing for numerous reasons. The solution to this problem is a system in which the placement machine can automatically detect and compensate for misalignment of the solder paste to produce high-quality boards regardless of the process errors beforehand.
Technical Library | 2023-09-05 21:00:53.0
The head on pillow defect is becoming more common. This paper describes one such occurrence for an OEM and explains how it was dealt with. In this particular case it was solved by application of problem solving skills by the OEM, component supplier and the solder paste provider
Technical Library | 2020-07-02 01:14:44.0
Head-in-Pillow (HIP) defects are a growing concern in the electronics industry. These defects are usually believed to be the result of several factors, individually or in combination. Some of the major contributing factors include: surface quality of the BGA spheres, activity of the paste flux, improper placement / misalignment of the components, a non-optimal reflow profile, and warpage of the components. To understand the role of each of these factors in producing head-in-pillow defects and to find ways to mitigate them, we have developed two in-house tests.
Technical Library | 2009-12-14 20:24:19.0
In the lead-free era, thermal profiling has a critical role in the SMT assembly process. We discuss the profiling, tools, practical issues, and inspection methods of golden boards, and related tools. As the process window narrows, profiling equipment and/or thermocouple (TC) errors must be taken into consideration. In addition, the accuracy and attachment method of the thermocouple will significantly impact critical assemblies.
Technical Library | 2009-11-05 11:17:32.0
Head-in-pillow (HiP), also known as ball-and-socket, is a solder joint defect where the solder paste deposit wets the pad, but does not fully wet the ball. This results in a solder joint with enough of a connection to have electrical integrity, but lacking sufficient mechanical strength. Due to the lack of solder joint strength, these components may fail with very little mechanical or thermal stress. This potentially costly defect is not usually detected in functional testing, and only shows up as a failure in the field after the assembly has been exposed to some physical or thermal stress.
Technical Library | 2019-08-15 13:31:52.0
Cracks in ceramic chip capacitors can be introduced at any process step during surface mount assembly. Thermal shock has become a "pat" answer for all of these cracks, but about 75 to 80% originate from other sources. These sources include pick and place machine centering jaws, vacuum pick up bit, board depanelization, unwarping boards after soldering, test fixtures, connector insulation, final assembly, as well as defective components. Each source has a unique signature in the type of crack that it develops so that each can be identified as the source of error.
Technical Library | 2016-05-13 11:44:16.0
The process of manufacturing and qualifying IC's consists of many steps while Temperature forcing systems play a crucial role in the final testing process. These environmental tests assure quality and reliability by stressing the device on one hand as well as helping to characterize and validate it on the other hand (making sure manufacturing outcome meets the design requirements). At later stages the temperature testing can support failure analysis effort and root cause analysis. AS common practice we are dealing with few different kinds of temperature forcing systems: Chambers, Thermal Stream systems and Direct Thermal Head systems. In this article I would like to focus on the practical aspects of utilizing Thermal Stream systems and Direct Thermal Head systems.
Technical Library | 2014-12-18 17:22:34.0
Manufacturing technology faces challenges with new packages/process when confronting the need for high yields. Identifying product defects associated with the manufacturing process is a critical part of electronics manufacturing. In this project, we focus on how to use AXI to identify BGA Head-in-Pillow (HIP), which is challenging for AXI testing. Our goal is to help us understand the capabilities of current AXI machines.