Technical Library | 2023-01-17 17:19:44.0
A test program was developed to evaluate the effectiveness of vacuum reflow processing on solder joint voiding and subsequent thermal cycling performance. Area array package test vehicles were assembled using conventional reflow processing and a solder paste that generated substantial void content in the solder joints. Half of the population of test vehicles then were re-processed (reflowed) using vacuum reflow. Transmission x-ray inspection showed a significant reduction in solder voiding after vacuum processing. The solder attachment reliability of the conventional and vacuum reflowed test vehicles was characterized and compared using two different accelerated thermal cycling profiles. The thermal cycling results are discussed in terms of the general impact of voiding on solder thermal fatigue reliability, results from the open literature, and the evolving industry standards for solder voiding. Recommendations are made for further work based on other void reduction methods and additional reliability studies.
Technical Library | 2021-07-20 20:02:29.0
During the manufacturing of printed circuit boards (PCBs) for a Flight Project, it was found that a European manufacturer was building its boards to a European standard that had no requirement for copper wrap on the vias. The amount of copper wrap that was measured on coupons from the panel containing the boards of interest was less than the amount specified in IPC-6012 Rev B, Class 3. To help determine the reliability and usability of the boards, three sets of tests and a simulation were run. The test results, along with results of simulation and destructive physical analysis, are presented in this paper. The first experiment involved subjecting coupons from the panels supplied by the European manufacturer to thermal cycling. After 17 000 cycles, the test was stopped with no failures. A second set of accelerated tests involved comparing the thermal fatigue life of test samples made from FR4 and polyimide with varying amounts of copper wrap. Again, the testing did not reveal any failures. The third test involved using interconnect stress test coupons with through-hole vias and blind vias that were subjected to elevated temperatures to accelerate fatigue failures. While there were failures, as expected, the failures were at barrel cracks. In addition to the experiments, this paper also discusses the results of finite-element analysis using simulation software that was used to model plated-through holes under thermal stress using a steady-state analysis, also showing the main failure mode was barrel cracking. The tests show that although copper wrap was sought as a better alternative to butt joints between barrel plating and copper foil layers, manufacturability remains challenging and attempts to meet the requirements often result in features that reduce the reliability of the boards. Experimental and simulation work discussed in this paper indicate that the standard requirements for copper wrap are not contributing to the overall board reliability, although it should be added that a design with a butt joint is going to be a higher risk than a reduced copper wrap design. The study further shows that procurement requirements for wrap plating thickness from Class 3 to Class 2 would pose little risk to reliability (minimum 5 μm/0.197 mil for all via types).Experimental results corroborated by modeling indicate that the stress maxima are internal to the barrels rather than at the wrap location. In fact, the existence of Cu wrap was determined to have no appreciable effect on reliability.
Technical Library | 2019-10-18 10:37:25.0
It usually does not make any logic to invest in costly fabrication equipment in case you just desire to spin some prototypes and rather outsource your Printed Circuit Board assembly as well as prototype fabrication to a trustworthy vendor. I would provide a few tips as to what to consider when seeking a contract manufacturer. The two most common procedures associated with Printed Circuit Board Assembly are through-hole technology and surface mount technology. Talking about the difference between through-hole technology and surface mount technology. Through-hole elements have metal leads, & these metal leads are supplied through-plated holes inside the circuit board. On the other hand, SMT elements might or might not have leads, nevertheless most significantly, they are developed to be soldered onto the surface of the circuit boards straight on the same side as the element body. A lot of contract manufacturers would provide a quick quote mechanism over their site for the fabrication of circuit boards as well as assembly of prototypes. This would bank your time when comparing various vendors. Ensure that the quote system facilitates you to fill your details, for instance, board material, thickness, copper thickness, milling, etc. in order that you can avail of a precise quote devoid of any surprises afterward. And this is quite necessary. Typically the cost per board would decline as quality upgrades. This is owing to the fairly high setup price of circuit board fabrication over and above component assembly. A few vendors would employ a system where they unite boards from various consumers. This manner the setup price would be circulated among numerous clients. When you fabricate an item, you clearly don’t desire to have to fabricate a big quantity of boards straight away whilst you improve your design. One restriction with small quantity prototypes though is that the option of materials & material thicknesses would be constrained. In case you are employing a particular material then opportunities are there will not be any other clients employing the same material. Additionally, lead time plays a major role in indecisive prices. A longer lead time facilitates the fabricator more liberty in slotting your fabrication. This is basically reflected in cheaper prices that would view in the quote section. Clearly, if you are in a hurry and desire to be moved to the summit of the pile you would require splurging more dollars. Ensure that your contract fabricator would support the file sort for producing which you offer. The most general format for printed circuit board fabrication is the Gerber format nonetheless a few vendors would moreover embrace board files from general printed circuit board software products. A few suppliers also provide in house printed circuit design. Even in case, you create your board yourself, choosing a vendor with design services might prove resourceful in case there is an issue with your files. In this scenario, your vendor could make swift changes that would neglect pricey delays. If you are looking for an Electronic Manufacturing Services (EMS Assembly) provider, then the web is the best to search.
| 1 |
Reflow ovens for automated SMT PCB assembly, specializing in lead free processing and nitrogen reflow. The best convection reflow ovens on the market.
4 Vreeland Rd.
Florham Park, NJ USA
Phone: 973-377-6800