Technical Library | 2022-10-04 16:43:10.0
In this paper I will discuss the different methods and equipment used to detect counterfeit electronic parts, specifically integrated circuits as well as demonstrate some of the "red flags" that help to identify a part as being suspected counterfeit. We will begin with the initial receipt of the parts and the examination of the outer packaging, the basic visual inspection of the parts, the visual inspection and documentation at high magnification, permanency marking, blacktop test, scrape test, XRF (RoHS), decapsulation, X-ray, basic electrical testing, C-SAM, full function testing and limited function testing.
Technical Library | 2021-09-21 20:20:22.0
The electronics industry has been using the epoxy puck for the processing of the vast majority of electronics microsections since the 1970s. Minimal advancements have been seen in the methods used for precision micro-sections of PCBs, PCBAs, and device packages. This paper will discuss different techniques and approaches in performing precision and analytical micro-sections, which fuse the techniques and materials common in preparation of silicon wafers and bulk materials. These techniques have not only been found to produce excellent optical results, but transfer effectively to SEM for high magnification inspection and further analysis with minimal post-lapping preparation needed. Additionally, processing time is reduced primarily due to a significant reduction of bulk material removal earlier in the preparation, therefore needing less removal at later lapping steps compared to traditional sectioning methods. Additional techniques are introduced that mitigate some classic challenges experienced by technicians over the decades.
Technical Library | 2023-11-20 18:49:11.0
Non-destructive testing during the manufacture of printed wiring boards (PWBs) has become ever more important for checking product quality without compromising productivity. Using x-ray inspection, not only provides a non-destructive test but also allows investigation within optically hidden areas, such as the quality of post solder reflow of area array devices (e.g. BGAs, CSPs and flip chips). As the size of components continues to diminish, today's x-ray inspection systems must provide increased magnification, as well as better quality x-ray images to provide the necessary analytical information. This has led to a number of x-ray manufacturers offering digital x-ray inspection systems, either as standard or as an option, to satisfy these needs. This paper will review the capabilities that these digital x-ray systems offer compared to their analogue counterparts. There is also a discussion of the various types of digital x-ray systems that are available and how the use of different digital detectors influences the operational capabilities that such systems provide.
Technical Library | 2020-08-27 01:22:45.0
Initially adopted internal specifications for acceptance of printed circuit boards (PCBs) used for wire bonding was that there were no nodules or scratches allowed on the wirebond pads when inspected under 20X magnification. The nodules and scratches were not defined by measurable dimensions and were considered to be unacceptable if there was any sign of a visual blemish on wire-bondable features. Analysis of the yield at a PCB manufacturer monitored monthly for over two years indicated that the target yield could not be achieved, and the main reasons for yield loss were due to nodules and scratches on the wirebonding pads. The PCB manufacturer attempted to eliminate nodules and scratches. First, a light-scrubbing step was added after electroless copper plating to remove any co-deposited fine particles that acted as a seed for nodules at the time of copper plating. Then, the electrolytic copper plating tank was emptied, fully cleaned, and filtered to eliminate the possibility of co-deposited particles in the electroplating process. Both actions greatly reduced the density of the nodules but did not fully eliminate them. Even though there was only one nodule on any wire-bonding pad, the board was still considered a reject. To reduce scratches on wirebonding pads, the PCB manufacturer utilized foam trays after routing the boards so that they did not make direct contact with other boards. This action significantly reduced the scratches on wire-bonding pads, even though some isolated scratches still appeared from time to time, which caused the boards to be rejected. Even with these significant improvements, the target yield remained unachievable. Another approach was then taken to consider if wire bonding could be successfully performed over nodules and scratches and if there was a dimensional threshold where wire bonding could be successful. A gold ball bonding process called either stand-off-stitch bonding (SSB) or ball-stitch-on-ball bonding (BSOB) was used to determine the effects of nodules and scratches on wire bonds. The dimension of nodules, including height, and the size of scratches, including width, were measured before wire bonding. Wire bonding was then performed directly on various sizes of nodules and scratches on the bonding pad, and the evaluation of wire bonds was conducted using wire pull tests before and after reliability testing. Based on the results of the wire-bonding evaluation, the internal specification for nodules and scratches for wirebondable PCBs was modified to allow nodules and scratches with a certain height and a width limitation compared to initially adopted internal specifications of no nodules and no scratches. Such an approach resulted in improved yield at the PCB manufacturer.
| 1 |